Measurement evidence
Mimicking the Electron Transport Chain and Active Site of [FeFe] Hydrogenases in One Metal-Organic Framework: Factors That Influence Charge Transport · Castner A.T., Johnson B.A., Cohen S.M. et al. · Journal of the American Chemical Society · 2021 · 7991-7999
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
PCN-700_NDI_FeFe powder · Powder
N2 adsorption at 77 K after activation at 85 C under active vacuum (1 x 10^-4 Pa).
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| PCN-700_NDI_FeFe BET surface area | BET Surface Area = 50.5 m2/g | — | — | Figure Axis Rounded Reported | p019 / SI p.19 · BET analysis · Figure S18 |
| PCN-700_NDI_FeFe isotherm type | Type IV isotherm with hysteresis | — | — | Caption Qualitative | p019 / SI p.19 · BET analysis · Figure S17 |
PCN-700_NDI_ta powder · Powder
N2 adsorption at 77 K after activation at 85 C under active vacuum (1 x 10^-4 Pa).
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| PCN-700_NDI_ta BET surface areaMarked as a best value within this paper | BET Surface Area = 990.7 m2/g | — | — | Figure Axis Rounded Reported | p018 / SI p.18 · BET analysis · Figure S16 |
PCN-700 MOF powder/crystals · Powder
N2 adsorption at 77 K after activation at 85 C under active vacuum (1 x 10^-4 Pa).
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| PCN-700 BET surface area | BET Surface Area = 729.7 m2/g | — | — | Figure Axis Rounded Reported | p017 / SI p.17 · BET analysis · Figure S14 |
| PCN-700 isotherm type | Type I isotherm | — | — | Caption Qualitative | p017 / SI p.17 · BET analysis · Figure S13 |