Other — Multifunctional coordination polymers based on copper(i) and mercaptonicotinic ligands: Synthesis, and structural, optical and electrical characterization

3 measurement groups · 3 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

CP1 orange solid from method A · Powder

PerkinElmer TGA7; 35-400 C under N2 gas flow; heating rate 5 C min^-1

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
thermal decomposition onset statement	thermal decomposition takes place at temperatures over 423 K	423 K	—	Text Approximate	5 · Electrical characterization · Figure S4

CP2 orange/red crystals · Single Crystal

PerkinElmer TGA7; 35-400 C under N2 gas flow; heating rate 5 C min^-1

Temperature: 308-673
Atmosphere: N2
Geometry: bulk crystals/powder
Context: pristine CP2
Measurement source: 3, 7 · Results and discussion; Experimental - Materials and methods · Figure S5

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
first TGA mass loss interval	Delta Y = 21.3166% from about 174.40 to 255.30 C	—	—	Visual Estimate Approximate	4 · TGA · Figure S5

CP3 yellow crystals from method A · Single Crystal

PerkinElmer TGA7; 35-400 C under N2 gas flow; heating rate 5 C min^-1

Temperature: 308-673
Atmosphere: N2
Geometry: bulk crystals/powder
Context: pristine CP3
Measurement source: 3, 7 · Results and discussion; Experimental - Materials and methods · Figure S6

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
first TGA mass loss interval	Delta Y = 5.5919% from about 168.47 to 225.37 C	—	—	Visual Estimate Approximate	4 · TGA · Figure S6