Electrical Transport — 1-Hydroxybenzotriazole (HOBt) acidity, formation constant with different metals and thermodynamic parameters: Synthesis and characterization of some HOBt metal complexes - Crystal structures of two polymers: [Cu2(H2O)5(OBt)2(μ-OBt)2] · 2H2O · EtOH (1A) and [Cu(μ-OBt)(HOBt)(OBt)(EtOH)] (1B)

11 measurement groups · 30 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

[Co(OBt)2(HOBt)2(H2O)2] pressed tablet · Pellet

294-423 K; two linear regimes fitted in Arrhenius form

Temperature: 294-423
Atmosphere: not stated
Geometry: pressed tablet between copper electrodes with silver paste
Context: pristine complex
Measurement source: 3534-3536 / rendered p009-p011 · 3.2.4 · Table 9; Fig. 8

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
DeltaE regime 1Marked as a best value within this paper	0.202	—	—	Table Exact Reported	3536 / rendered p011 · Table 9 · Table 9
DeltaE regime 2	0.375	—	—	Table Exact Reported	3536 / rendered p011 · Table 9 · Table 9
log sigma0 regime 1	4.142	—	—	Table Exact Reported	3536 / rendered p011 · Table 9 · Table 9
log sigma0 regime 2	5.33	—	—	Table Exact Reported	3536 / rendered p011 · Table 9 · Table 9
DeltaE-log sigma0 empirical fit	DeltaE = 6.8671 log sigma0 + 2.7549	—	—	Text Exact Reported	3535 / rendered p010 · 3.2.4 · Equations 22-24

[Cu(OBt)2(H2O)2] pressed tablet · Pellet

294-423 K; two linear regimes fitted in Arrhenius form

Temperature: 294-423
Atmosphere: not stated
Geometry: pressed tablet between copper electrodes with silver paste
Context: pristine complex
Measurement source: 3534-3536 / rendered p009-p011 · 3.2.4 · Table 9; Fig. 8

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
DeltaE regime 1Marked as a best value within this paper	0.254	—	—	Table Exact Reported	3536 / rendered p011 · Table 9 · Table 9
DeltaE regime 2	0.535	—	—	Table Exact Reported	3536 / rendered p011 · Table 9 · Table 9
log sigma0 regime 1	3.721	—	—	Table Exact Reported	3536 / rendered p011 · Table 9 · Table 9
log sigma0 regime 2	5.421	—	—	Table Exact Reported	3536 / rendered p011 · Table 9 · Table 9
DeltaE-log sigma0 empirical fit	DeltaE = 6.0498 log sigma0 + 2.1843	—	—	Text Exact Reported	3535 / rendered p010 · 3.2.4 · Equations 22-24

HOBt solid control · Powder

294-423 K; tablets pressed at 4 tons/cm2, area 1.37 cm2, thickness 0.12 mm; copper electrodes with silver paste; current sensitivity to 1e-15 A

Temperature: 294-423
Atmosphere: not stated
Geometry: pressed tablet between copper electrodes with silver paste
Context: pristine ligand control
Measurement source: 3528 and 3536 / rendered p003,p011 · 2.2; 3.2.4 · Table 9; Fig. 8

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
DeltaE regime 1Marked as a best value within this paper	0.825	—	—	Table Exact Reported	3536 / rendered p011 · Table 9 · Table 9
DeltaE regime 2	0.222	—	—	Table Exact Reported	3536 / rendered p011 · Table 9 · Table 9
DeltaE regime 3	0.796	—	—	Table Exact Reported	3536 / rendered p011 · Table 9 · Table 9
log sigma0 regime 1	5.367	—	—	Table Exact Reported	3536 / rendered p011 · Table 9 · Table 9
log sigma0 regime 2	5.944	—	—	Table Exact Reported	3536 / rendered p011 · Table 9 · Table 9
log sigma0 regime 3	12.488	—	—	Table Exact Reported	3536 / rendered p011 · Table 9 · Table 9

[Ni(OBt)(Cl)(H2O)2] pressed tablet · Pellet

294-423 K; multiple linear regimes fitted in Arrhenius form

Temperature: 294-423
Atmosphere: not stated
Geometry: pressed tablet between copper electrodes with silver paste
Context: pristine complex
Measurement source: 3534-3536 / rendered p009-p011 · 3.2.4 · Table 9; Fig. 8

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
DeltaE regime 1Marked as a best value within this paper	0.301	—	—	Table Exact Reported	3536 / rendered p011 · Table 9 · Table 9
DeltaE regime 2	0.522	—	—	Table Exact Reported	3536 / rendered p011 · Table 9 · Table 9
DeltaE regime 3	0.821	—	—	Table Exact Reported	3536 / rendered p011 · Table 9 · Table 9
log sigma0 regime 1	5.62	—	—	Table Exact Reported	3536 / rendered p011 · Table 9 · Table 9
log sigma0 regime 2	6.74	—	—	Table Exact Reported	3536 / rendered p011 · Table 9 · Table 9
log sigma0 regime 3	8.611	—	—	Table Exact Reported	3536 / rendered p011 · Table 9 · Table 9
DeltaE-log sigma0 empirical fit	DeltaE = 5.7808 log sigma0 + 3.8225	—	—	Text Exact Reported	3535 / rendered p010 · 3.2.4 · Equations 22-24