Porosity — Cation-dependent intrinsic electrical conductivity in isostructural tetrathiafulvalene-based microporous metal-organic frameworks

4 measurement groups · 7 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

desolvated Cd2(TTFTB) · Powder

Micromeritics ASAP 2020; sample outgassed under vacuum until outgas rate <2 mtorr/min; N2 isotherm measured at 77 K.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Cd2(TTFTB) BET surface area	521	—	—	Text Rounded Reported	p002 / article p.1775 · Results · Figure S4
Cd2(TTFTB) N2 uptake at 77 K	~140	—	—	Text Approximate	p002 / article p.1775 · Results · Figure S4

desolvated Co2(TTFTB) · Powder

Micromeritics ASAP 2020; sample outgassed under vacuum until outgas rate <2 mtorr/min; N2 isotherm measured at 77 K.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Co2(TTFTB) BET surface area	531	—	—	Text Rounded Reported	p002 / article p.1775 · Results · Figure S4
Co2(TTFTB) N2 uptake at 77 K	~170	—	—	Text Approximate	p002 / article p.1775 · Results · Figure S4

desolvated Mn2(TTFTB) · Powder

Micromeritics ASAP 2020; sample outgassed under vacuum until outgas rate <2 mtorr/min; N2 isotherm measured at 77 K.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Mn2(TTFTB) BET surface area	470	—	—	Text Rounded Reported	p002 / article p.1775 · Results · Figure S4
Mn2(TTFTB) N2 uptake at 77 K	~150	—	—	Text Approximate	p002 / article p.1775 · Results · Figure S4

desolvated Zn2(TTFTB) reference sample · Powder

Micromeritics ASAP 2020; sample outgassed under vacuum until outgas rate <2 mtorr/min; N2 isotherm measured at 77 K.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Zn2(TTFTB) reported BET surface area	537	—	—	Text Rounded Reported	p002 / article p.1775 · Results