Other — Copper(i) iodide coordination polymers with triazole substituted pyridine ligands: photophysical and electrical conductivity properties

3 measurement groups · 9 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

CP1 bulk powder · Powder

N2 flow 20 mL min^-1; heating rate 10 deg C min^-1; range 30-800 deg C

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
first weight loss	approximately 42%; Fig. S15 label 41.44%	—	approximately	Text Approximate	4 · Thermogravimetric analysis · Fig. S15
second weight loss	33%	—	—	Text Rounded Reported	4 · Thermogravimetric analysis · Fig. S15
first degradation onset	158 deg C	—	—	Text Rounded Reported	4 · Thermogravimetric analysis · Fig. S15

CP2 bulk powder · Powder

N2 flow 20 mL min^-1; heating rate 10 deg C min^-1; range 30-800 deg C

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
first weight loss	40.26%	—	—	Visual Estimate Approximate	18 · TGA · Fig. S16
second weight loss	31.88%	—	—	Visual Estimate Approximate	18 · TGA · Fig. S16
first degradation onset	183 deg C	—	—	Text Rounded Reported	4 · Thermogravimetric analysis · Fig. S16

CP3 bulk yellow powder · Powder

N2 flow 20 mL min^-1; heating rate 10 deg C min^-1; range 30-800 deg C

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
first weight loss	40.13%	—	—	Visual Estimate Approximate	18 · TGA · Fig. S17
second weight loss	32.25%	—	—	Visual Estimate Approximate	18 · TGA · Fig. S17
first degradation onsetMarked as a best value within this paper	194 deg C	—	—	Text Rounded Reported	4 · Thermogravimetric analysis · Fig. S17