Electrical Transport — Synthesis, conductivity, and electromagnetic wave absorption properties of chiral poly Schiff bases and their silver complexes

9 measurement groups · 9 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Room-temperature conductivity; RTS-8x four-probe apparatus for higher-conductivity range and AS-31356 AC conductivity tester with copper contacts for low-conductivity range.

Electrical conductivity

Complex 1a pressed tablet / dried black powder · Pellet

Pressed tablet, approximately 1 mm thick, prepared at 15 MPa; room temperature.

Temperature: room temperature
Atmosphere: ambient/not specified
Geometry: pressed tablet with electrical contacts
Context: neat polymer or neat silver complex
Measurement source: 2 · Measurements

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
room-temperature electrical conductivity	7.2 x 10^-4 S/cm	—	—	Table Exact Reported	4 · Conductivity Analysis · Table I

Room-temperature conductivity; RTS-8x four-probe apparatus for higher-conductivity range and AS-31356 AC conductivity tester with copper contacts for low-conductivity range.

Electrical conductivity

Complex 1b pressed tablet / dried black powder · Pellet

Pressed tablet, approximately 1 mm thick, prepared at 15 MPa; room temperature.

Temperature: room temperature
Atmosphere: ambient/not specified
Geometry: pressed tablet with electrical contacts
Context: neat polymer or neat silver complex
Measurement source: 2 · Measurements

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
room-temperature electrical conductivity	2.4 x 10^-4 S/cm	—	—	Table Exact Reported	4 · Conductivity Analysis · Table I

Room-temperature conductivity; RTS-8x four-probe apparatus for higher-conductivity range and AS-31356 AC conductivity tester with copper contacts for low-conductivity range.

Electrical conductivity

Complex 2a pressed tablet / dried black powder · Pellet

Pressed tablet, approximately 1 mm thick, prepared at 15 MPa; room temperature.

Temperature: room temperature
Atmosphere: ambient/not specified
Geometry: pressed tablet with electrical contacts
Context: neat polymer or neat silver complex
Measurement source: 2 · Measurements

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
room-temperature electrical conductivity	1.3 x 10^-5 S/cm	—	—	Table Exact Reported	4 · Conductivity Analysis · Table I

Room-temperature conductivity; RTS-8x four-probe apparatus for higher-conductivity range and AS-31356 AC conductivity tester with copper contacts for low-conductivity range.

Electrical conductivity

Complex 3a pressed tablet / dried brown powder · Pellet

Pressed tablet, approximately 1 mm thick, prepared at 15 MPa; room temperature.

Temperature: room temperature
Atmosphere: ambient/not specified
Geometry: pressed tablet with electrical contacts
Context: neat polymer or neat silver complex
Measurement source: 2 · Measurements

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
room-temperature electrical conductivity	11.7 S/cm	—	—	Table Exact Reported	4 · Conductivity Analysis · Table I

Room-temperature conductivity; RTS-8x four-probe apparatus for higher-conductivity range and AS-31356 AC conductivity tester with copper contacts for low-conductivity range.

Electrical conductivity

Complex 4a pressed tablet / dried black powder · Pellet

Pressed tablet, approximately 1 mm thick, prepared at 15 MPa; room temperature.

Temperature: room temperature
Atmosphere: ambient/not specified
Geometry: pressed tablet with electrical contacts
Context: neat polymer or neat silver complex
Measurement source: 2 · Measurements

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
room-temperature electrical conductivityMarked as a best value within this paper	3.7 x 10^2 S/cm	—	—	Table Exact Reported	4 · Conductivity Analysis · Table I

Room-temperature conductivity; RTS-8x four-probe apparatus for higher-conductivity range and AS-31356 AC conductivity tester with copper contacts for low-conductivity range.

Electrical conductivity

Polymer 1 pressed tablet / dried gray powder · Pellet

Pressed tablet, approximately 1 mm thick, prepared at 15 MPa; room temperature.

Temperature: room temperature
Atmosphere: ambient/not specified
Geometry: pressed tablet with electrical contacts
Context: neat polymer or neat silver complex
Measurement source: 2 · Measurements

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
room-temperature electrical conductivity	3.7 x 10^-10 S/cm	—	—	Table Exact Reported	4 · Conductivity Analysis · Table I

Room-temperature conductivity; RTS-8x four-probe apparatus for higher-conductivity range and AS-31356 AC conductivity tester with copper contacts for low-conductivity range.

Electrical conductivity

Polymer 2 pressed tablet / dried brown powder · Pellet

Pressed tablet, approximately 1 mm thick, prepared at 15 MPa; room temperature.

Temperature: room temperature
Atmosphere: ambient/not specified
Geometry: pressed tablet with electrical contacts
Context: neat polymer or neat silver complex
Measurement source: 2 · Measurements

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
room-temperature electrical conductivity	8.0 x 10^-11 S/cm	—	—	Table Exact Reported	4 · Conductivity Analysis · Table I

Room-temperature conductivity; RTS-8x four-probe apparatus for higher-conductivity range and AS-31356 AC conductivity tester with copper contacts for low-conductivity range.

Electrical conductivity

Polymer 3 pressed tablet / dried buff powder · Pellet

Pressed tablet, approximately 1 mm thick, prepared at 15 MPa; room temperature.

Temperature: room temperature
Atmosphere: ambient/not specified
Geometry: pressed tablet with electrical contacts
Context: neat polymer or neat silver complex
Measurement source: 2 · Measurements

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
room-temperature electrical conductivity	2.4 x 10^-10 S/cm	—	—	Table Exact Reported	4 · Conductivity Analysis · Table I

Room-temperature conductivity; RTS-8x four-probe apparatus for higher-conductivity range and AS-31356 AC conductivity tester with copper contacts for low-conductivity range.

Electrical conductivity

Polymer 4 pressed tablet / dried gray powder · Pellet

Pressed tablet, approximately 1 mm thick, prepared at 15 MPa; room temperature.

Temperature: room temperature
Atmosphere: ambient/not specified
Geometry: pressed tablet with electrical contacts
Context: neat polymer or neat silver complex
Measurement source: 2 · Measurements

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
room-temperature electrical conductivity	3.9 x 10^-10 S/cm	—	—	Table Exact Reported	4 · Conductivity Analysis · Table I