Other — Promoting electromagnetic wave absorption for conductive metal-organic frameworks through crystal morphology controlling

2 measurement groups · 3 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Ni-TABQ-1 black crystalline powder · Powder

Thermal stability under air, heating rate 20 C min-1 from room temperature to 800 C.

Atmosphere: air
Context: pristine Ni-TABQ-1 powder
Measurement source: main p.2 / journal p.11526 · Characterization · Fig. S2a

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Framework skeleton breakdown onset	approximately 350 C	—	—	Text Approximate	main p.3 / journal p.11527 · Results and discussion · Fig. S2a-b
Weight loss, 30-150 C	about 3.1%	—	—	Text Approximate	main p.3 / journal p.11527 · Results and discussion · Fig. S2a

Ni-TABQ-2 black powder · Powder

Thermal stability under air, heating rate 20 C min-1 from room temperature to 800 C.

Atmosphere: air
Context: pristine Ni-TABQ-2 powder
Measurement source: main p.2 / journal p.11526 · Characterization · Fig. S2b

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Weight loss, 30-150 C	approximately 6.3%	—	—	Text Approximate	main p.3 / journal p.11527 · Results and discussion · Fig. S2b