Diffraction Structure — Carbon quantum dot-mediated binary metal-organic framework nanosheets for efficient oxygen evolution at ampere-level current densities in proton exchange membrane electrolyzers

Measurement evidence

Diffraction Structure

Carbon quantum dot-mediated binary metal-organic framework nanosheets for efficient oxygen evolution at ampere-level current densities in proton exchange membrane electrolyzers · Ni Q., Zhang S., Wang K. et al. · Journal of Materials Chemistry A · 2024 · 31253-31261

1 measurement group · 2 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Powder X-ray diffraction

X-ray diffraction and scattering

NiFe-MOF-CQD · Nanosheet

XRD patterns of NiFe-MOF, NiFe-MOF-CQD and CQD supporting pattern.

Context: target composite compared with pristine NiFe-MOF
Measurement source: 31255 and 31257 · Results and discussion · Figure 3a; Figure S4a

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
CQD-related broad XRD peak	around 20 degrees, assigned to CQD (002)	—	—	Text Approximate	31255 · Results and discussion · Figure 3a; Figure S4a
NiFe-MOF/NiFe-MOF-CQD main XRD peaks	33, 38 and 59 degrees 2theta	—	—	Text Rounded Reported	31255 · Results and discussion · Figure 3a