Porosity — Particle size dependence of proton conduction in a cationic lanthanum phosphonate MOF

Measurement evidence

Porosity

Particle size dependence of proton conduction in a cationic lanthanum phosphonate MOF · Levenson D.A., Zhang J., Gelfand B.S. et al. · Dalton Transactions · 2020 · 4022-4029

1 measurement group · 1 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

195 K CO2 adsorption

Gas sorption and porosity

as-synthesised PCMOF21-AcO bulk powder · Powder

PCMOF21-AcO activated at 100 deg C overnight; adsorption isotherm shown in SI Figure S11.

Temperature: 195
Atmosphere: CO2
Geometry: gas adsorption isotherm
Context: pristine activated framework
Measurement source: p007 · Figure S11 caption · Figure S11

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
CO2 uptake at high relative pressure	approximately 0.19-0.20 mmol/g near P/P0 0.9	—	—	Visual Estimate Approximate	p007 · Figure S11 · Figure S11