Measurement evidence
Spin crossover in Fe(triazole)-Pt nanoparticle self-assembly structured at the sub-5 nm scale · Usmani S., Mikolasek M., Gillet A. et al. · Nanoscale · 2020 · 8180-8187
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
Pristine PtNP deposit on electrode · Electrode
Pristine PtNP deposit measured at 300 K.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Pristine PtNP I-V response | linear I-V at 300 K | — | — | Visual Estimate Qualitative | p005 · Supplementary information · Fig. S4a |
| Pristine PtNP current near +2 V | approximately +750 nA at +2 V | — | visual estimate from axis | Figure Axis Approximate | p005 · Supplementary information · Fig. S4a |
PtNPs-FeL3 self-assembly drop-cast on interdigitated electrodes · Electrode
PtNPs-FeL3 self-assembly measured at 300 K; non-linearity used as Coulomb blockade signature.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Self-assembly I-V non-linearityMarked as a best value within this paper | non-linear I-V, signature of Coulomb blockade | — | — | Caption Qualitative | p005 · Supplementary information · Fig. S4b |
| Self-assembly current near +2.5 V | approximately +58 nA at +2.5 V | — | visual estimate from axis | Figure Axis Approximate | p005 · Supplementary information · Fig. S4b |
PtNPs-FeL3 self-assembly drop-cast on interdigitated electrodes · Electrode
Electrode biased at 0.1 V with temperature sweep rate of 3 K min^-1.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Bias voltage for hysteresis-like current-temperature cycle | 0.1 V | — | — | Caption Exact Reported | p007 · Supplementary information · Fig. S6 |
| Approximate current near 300 K in hysteresis plot | approximately 150 nA near 300 K | — | visual estimate from axis | Figure Axis Approximate | p007 · Supplementary information · Fig. S6 |
| Sweep rate for hysteresis-like current-temperature cycle | 3 K min^-1 | — | — | Caption Exact Reported | p007 · Supplementary information · Fig. S6 |
PtNPs-FeL3 self-assembly drop-cast on interdigitated electrodes · Electrode
Drop-cast SA on interdigitated electrodes; nitrogen-cooled cryostat; Keithley 6430 subfemtoamperemeter; temperature swept at 1 K min^-1 unless otherwise stated.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Transport current range | few nA to few hundred nA | — | — | Text Range | p005, journal p. 8184 · Magnetic and charge transport measurements · ESI Fig. S5 |
| Current-temperature slope breakMarked as a best value within this paper | around 280 K | — | — | Caption Approximate | p004, journal p. 8183 · Magnetic and charge transport measurements · Fig. 4b |
| Hybrid assembly resistance rangeMarked as a best value within this paper | 10-10^3 Mohm | — | — | Text Range | p005, journal p. 8184 · Magnetic and charge transport measurements · ESI Fig. S5 |
| Slope breaks on independent electrodes | around 270 K | — | — | Caption Approximate | p006 · Supplementary information · Fig. S5 |
| Electrodes showing slope break | four out of six measured electrodes | 0.667 fraction of measured electrodes | — | Text Exact Reported | p007, journal p. 8186 · Charge transport measurements |
| Transport voltage range | few tenths of a volt up to 2 V | — | — | Text Range | p005, journal p. 8184 · Magnetic and charge transport measurements · ESI Fig. S5 |