Measurement evidence
The Different Roles of Cobalt and Manganese in Metal-Organic Frameworks for Supercapacitors · Iqbal R., Sultan M.Q., Hussain S. et al. · Advanced Materials Technologies · 2021 · 2000941
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
Co3(HITP)2 bulk powder · Powder
N2 sorption at 77 K; samples outgassed at 150 degrees C for 6 h under 10-6 Torr before adsorption according to SI.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| BET surface area | 856 m2 g-1 | — | — | Text Rounded Reported | p003-p004 · Results and Discussion · Figure 3c |
| Unique pore size | 1.3 nm | — | — | Text Rounded Reported | p004 · Results and Discussion · Figure 3a |
Co-MOF exfoliated nanosheets · Nanosheet
N2 sorption at 77 K after exfoliation.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| BET surface areaMarked as a best value within this paper | 2338 m2 g-1 | — | — | Text Rounded Reported | p004 · Results and Discussion · Figure 3c |
Mn3(HITP)2 bulk powder · Powder
N2 sorption at 77 K; samples outgassed at 150 degrees C for 6 h under 10-6 Torr before adsorption according to SI.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| BET surface area | 843 m2 g-1 | — | — | Text Rounded Reported | p003-p004 · Results and Discussion · Figure 3d |
| Unique pore size | 1.6 nm | — | — | Text Rounded Reported | p004 · Results and Discussion · Figure 3b |
Mn-MOF exfoliated nanosheets · Nanosheet
N2 sorption at 77 K after exfoliation.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| BET surface areaMarked as a best value within this paper | 2302 m2 g-1 | — | — | Text Rounded Reported | p004 · Results and Discussion · Figure 3d |