Porosity — Synthesis, structure, and lithium storage performance of non-conductive metal–organic frameworks for high-performance lithium-ion batteries

2 measurement groups · 6 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Ni-mba-K product · Powder

Micromeritics ASAP 2020M, liquid nitrogen temperature (-196 deg C), BET equation

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET specific surface area from SI figure labelMarked as a best value within this paper	Sbet = 2.8310 m2/g	—	—	Figure Axis Rounded Reported	S2 · Supporting Information · Figure S3(b)
hierarchical pore description	hierarchical pores from microporous to mesoporous/macroporous	—	—	Qualitative Qualitative	3 · 3.1. Structural characterization · Figs. S3(a), S3(b)
specific surface area	<10 m2 g-1	—	less than	Text Range	3 · 3.1. Structural characterization · Fig. S3(b)

Ni-mba-Na black fibrous product · Powder

Micromeritics ASAP 2020M, liquid nitrogen temperature (-196 deg C), BET equation

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET specific surface area from SI figure label	Sbet = 2.6944 m2/g	—	—	Figure Axis Rounded Reported	S2 · Supporting Information · Figure S3(a)
hierarchical pore description	hierarchical pores from microporous to mesoporous/macroporous	—	—	Qualitative Qualitative	3 · 3.1. Structural characterization · Figs. S3(a), S3(b)
specific surface area	<10 m2 g-1	—	less than	Text Range	3 · 3.1. Structural characterization · Fig. S3(a)