Other — Mn2(2,5-disulfhydrylbenzene-1,4-dicarboxylate): A microporous metal-organic framework with infinite (-Mn-S-)∞ chains and high intrinsic charge mobility

2 measurement groups · 4 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

As-synthesized 1 powder · Powder

TA Instruments Q500, 2 deg C/min under N2 flow of 90 mL/min.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
As-synthesized absorbed DMF loss annotation	31.83% absorbed DMF loss	—	—	Visual Estimate Rounded Reported	SI p.S8 · Figure S1 · Figure S1
As-synthesized TGA mass lossMarked as a best value within this paper	31.8% between 50 and 365 deg C	—	—	Text Rounded Reported	main p.8186 · Main text, TGA · Figure S1

Methanol-exchanged 1 powder · Powder

TA Instruments Q500, 2 deg C/min under N2 flow; held at 100 deg C and 150 deg C for 30 min.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Methanol-exchanged absorbed MeOH loss annotationMarked as a best value within this paper	26.73% absorbed MeOH loss	—	—	Visual Estimate Rounded Reported	SI p.S9 · Figure S2 · Figure S2
Methanol-exchanged stable TGA plateau	stable plateau between 150 and 400 deg C	—	range 150-400 deg C	Text Range	main p.8187 · Main text, activation · Figure S2