Thermogravimetric analysis
HoHHTP powder · Powder
TGA at 3.0 K/min under 5 mL/min nitrogen flow on platinum pan.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|
Other — Efficient and tunable one-dimensional charge transport in layered lanthanide metal–organic frameworks
Measurement evidence
Other
Efficient and tunable one-dimensional charge transport in layered lanthanide metal–organic frameworks · Skorupskii G., Trump B.A., Kasel T.W. et al. · Nature Chemistry · 2020 · 131-136
4 measurement groups · 3 results
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
Thermogravimetric analysis
LaHHTP powder · Powder
TGA at 3.0 K/min under 5 mL/min nitrogen flow on platinum pan.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| framework decomposition onset | starts above 380 K and continues until full decomposition at 1100 K | — | — | Text Approximate | SI p.4 · Thermogravimetric and elemental analysis · Supplementary Figs. 2-5 |
| full decomposition temperature | 1100 K | — | — | Text Approximate | SI p.4 · Thermogravimetric and elemental analysis · Supplementary Figs. 2-5 |
| guest-solvent elimination temperature | before 380 K | — | — | Text Approximate | SI p.4 · Thermogravimetric and elemental analysis · Supplementary Figs. 2-5 |
Thermogravimetric analysis
NdHHTP powder · Powder
TGA at 3.0 K/min under 5 mL/min nitrogen flow on platinum pan.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|
Thermogravimetric analysis
YbHHTP powder · Powder
TGA at 3.0 K/min under 5 mL/min nitrogen flow on platinum pan.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|