Measurement evidence
Million-fold electrical conductivity enhancement in Fe2(DEBDC) versus Mn2(DEBDC) (E = S, O) · Sun L., Hendon C.H., Minier M.A. et al. · Journal of the American Chemical Society · 2015 · 6164-6167
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
Fe2(DOBDC)(DMF)2 · Pellet
Outgassed at 100 degC; N2 adsorption at 77 K.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| BET surface area | 241 m2/g | — | — | Text Exact Reported | 6165 · main text · Figure S8 |
Fe2(DSBDC)(DMF)2 · Pellet
Outgassed at 100 degC until outgas rate <2 mtorr/min; N2 adsorption at 77 K.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| BET surface area | 54 m2/g | — | — | Text Exact Reported | 6165 · main text · Figure S8 |
Mn2(DOBDC)(DMF)2 · Pellet
Outgassed at 100 degC; N2 adsorption at 77 K.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| BET surface areaMarked as a best value within this paper | 287 m2/g | — | — | Text Exact Reported | 6165 · main text · Figure S8 |
| N2 uptake at P/P0 approx. 0.9Marked as a best value within this paper | ca. 76 cm3/g at P/P0 approx. 0.9 | — | visual estimate from plotted axis | Figure Axis Approximate | S18 · Figure S8 · Figure S8 |
Mn2(DSBDC)(DMF)2 · Pellet
Outgassed at 100 degC; N2 adsorption at 77 K.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| BET surface area | 232 m2/g | — | — | Text Exact Reported | 6165 · main text · Figure S8 |