Construction of a Succinate-Bridged Cd(II)-Based Two-Dimensional Coordination Polymer for Efficient Optoelectronic Device Fabrication and Explosive Sensing Application · Dutta B., Hazra A., Dey A. et al. · Crystal Growth and Design · 2020 · 765-776

1 measurement group · 5 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Thermogravimetric analysis on PerkinElmer Pyris Diamond TG/DTA

Calorimetry and thermal analysis Thermogravimetric analysis

As-synthesised bulk compound 1 powder/crystals · Powder

30-600 deg C under nitrogen, flow rate 50 cm3 min-1, heating rate 2 deg C/min.

Temperature: 303-873
Atmosphere: N2
Geometry: bulk powder
Context: pristine compound 1
Measurement source: 766-767 · General Methods; Thermal Stability and Purity · Figure S4

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
First TGA weight loss	2.08% observed; 2.51% calculated	—	—	Text Exact Reported	767 · Thermal Stability and Purity · Figure S4
Calculated lattice-water weight loss	2.51% calculated	—	—	Text Exact Reported	767 · Thermal Stability and Purity · Figure S4
TGA first loss upper temperature	125 deg C	—	—	Text Exact Reported	767 · Thermal Stability and Purity · Figure S4
TGA first loss lower temperature	80 deg C	—	—	Text Exact Reported	767 · Thermal Stability and Purity · Figure S4
Thermal stability limit before decomposition	stable up to 250 deg C; starts decomposing after 250 deg C	—	—	Text Rounded Reported	767 · Thermal Stability and Purity · Figure S4