Porosity — From n- To p-Type Material: Effect of Metal Ion on Charge Transport in Metal-Organic Materials

3 measurement groups · 6 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Ni-HITP powder · Powder

N2 isotherms at 77 K after pore clearing and vacuum activation.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Ni-HITP BET surface area from SI figure legendMarked as a best value within this paper	251.3800 m2/g	251.38 m2 g-1	—	Figure Axis Exact Reported	p007 · Figure S10 · Figure S10
Ni-HITP BET surface area	250 m2/g	250 m2 g-1	—	Text Rounded Reported	p003 · Results · Figure 1d

a-Pd-HITP powder · Powder

SI N2 isotherm for MOG analogues; value read from figure legend.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Pd-HITP BET surface area from SI figure legend	147.9953 m2/g	147.9953 m2 g-1	—	Figure Axis Exact Reported	p007 · Figure S10 · Figure S10

a-Pt-HITP powder · Powder

N2 isotherms at 77 K after pore clearing and vacuum activation.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
a-Pt-HITP BET surface area from SI figure legendMarked as a best value within this paper	66.5334 m2/g	66.5334 m2 g-1	—	Figure Axis Exact Reported	p007 · Figure S10 · Figure S10
a-Pt-HITP BET surface area	67 m2/g	67 m2 g-1	—	Text Rounded Reported	p003 · Results · Figure 1d
a-Pt-HITP isotherm type	Type IVa isotherm with Type H3 hysteresis loop	—	—	Text Qualitative	p003 · Results · Figure 1d