Measurement evidence
Mixed-metallic MOF based electrode materials for high performance hybrid supercapacitors · Jiao Y., Pei J., Chen D. et al. · Journal of Materials Chemistry A · 2017 · 1094-1102
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
Co/Ni-MOF NAFLs · Nanosheet
Dissolved in HNO3 mixture; ICP by Perkin Elmer Optima 5300DV.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Co atomic percentage by ICPMarked as a best value within this paper | 23 | — | — | SI Table Exact Reported | p005 · Table S1 · Table S1 |
| Ni atomic percentage by ICP | 77 | — | — | SI Table Exact Reported | p005 · Table S1 · Table S1 |
| Zn atomic percentage by ICP | 0 | — | — | SI Table Exact Reported | p005 · Table S1 · Table S1 |
Ni-MOF powder / NAFL control · Nanosheet
Dissolved in HNO3 mixture; ICP by Perkin Elmer Optima 5300DV.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Co atomic percentage by ICP | 0 | — | — | SI Table Exact Reported | p005 · Table S1 · Table S1 |
| Ni atomic percentage by ICP | 100 | — | — | SI Table Exact Reported | p005 · Table S1 · Table S1 |
| Zn atomic percentage by ICP | 0 | — | — | SI Table Exact Reported | p005 · Table S1 · Table S1 |
Zn/Ni-MOF NAFLs · Nanosheet
Dissolved in HNO3 mixture; ICP by Perkin Elmer Optima 5300DV.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Co atomic percentage by ICP | 0 | — | — | SI Table Exact Reported | p005 · Table S1 · Table S1 |
| Ni atomic percentage by ICP | 78 | — | — | SI Table Exact Reported | p005 · Table S1 · Table S1 |
| Zn atomic percentage by ICPMarked as a best value within this paper | 22 | — | — | SI Table Exact Reported | p005 · Table S1 · Table S1 |
Co/Ni-MOF NAFLs · Nanosheet
Room temperature to 800 C; 5 C min-1 reported for results discussion.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Primary organic-component decomposition onset/peak temperatureMarked as a best value within this paper | 400 | — | — | Text Rounded Reported | p004 / 1097 · Results and discussion · Fig. S2a-c |
Ni-MOF powder / NAFL control · Nanosheet
Room temperature to 800 C; 5 C min-1 reported for results discussion.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Primary organic-component decomposition onset/peak temperature | 345 | — | — | Text Rounded Reported | p004 / 1097 · Results and discussion · Fig. S2a-c |
Zn/Ni-MOF NAFLs · Nanosheet
Room temperature to 800 C; 5 C min-1 reported for results discussion.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Primary organic-component decomposition onset/peak temperature | 367 | — | — | Text Rounded Reported | p004 / 1097 · Results and discussion · Fig. S2a-c |