Other — Fluorescent metal-organic frameworks for selective sensing of toxic cations (Tl3+, Hg2+) and highly oxidizing anions ((CrO4)2−, (Cr2O7)2−, (MnO4)−)

3 measurement groups · 6 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

compound I yellow platelike crystals · Single Crystal

Magnetic behaviour measured from 300-2 K; room-temperature susceptibility at 1000 Oe; Curie-Weiss fit over 50-300 K.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Room-temperature chiMT at 1000 Oe	17.34 emu mol^-1 K	—	—	Text Rounded Reported	p004 / article p.1156 · Magnetic Studies · Figure 3
Curie-Weiss theta_p	-36.41 K	—	—	Text Rounded Reported	p004 / article p.1156 · Magnetic Studies · Figure 3
Modified Fisher fit exponent tau	0.859	—	—	Text Exact Reported	p004 / article p.1156 · Magnetic Studies · Figure 3

compound I yellow platelike crystals · Single Crystal

Oxygen atmosphere, 40 mL min^-1 flow, 30-800 C, 10 C min^-1 heating rate.

Atmosphere: oxygen
Geometry: powder/crystals
Context: pristine MOF
Measurement source: p003 / article p.1155 · Thermogravimetric Analysis · Figure S8 referenced

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Second/broad TGA weight loss	approximately 59.4% in 350-550 C	—	—	Text Approximate	p003 / article p.1155 · Thermogravimetric Analysis · Figure S8 referenced
First TGA weight loss	29% in 245-350 C	—	—	Text Rounded Reported	p003 / article p.1155 · Thermogravimetric Analysis · Figure S8 referenced

compound II yellow needlelike crystals · Single Crystal

Oxygen atmosphere, 40 mL min^-1 flow, 30-800 C, 10 C min^-1 heating rate.

Atmosphere: oxygen
Geometry: powder/crystals
Context: pristine MOF
Measurement source: p003 / article p.1155 · Thermogravimetric Analysis · Figure S8 referenced

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Total TGA weight loss	approximately 65%	—	—	Text Approximate	p003 / article p.1155 · Thermogravimetric Analysis · Figure S8 referenced