Electrical Transport — Paramagnetic Conducting Metal–Organic Frameworks with Three-Dimensional Structure

3 measurement groups · 9 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Co-THBQ pressed cuboid pellet · Pellet

Pressed cuboid pellet measured with KEITHLEY 2002 multimeter; temperature range 300-400 K.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
activation energy from Arrhenius conductivity	0.46 eV	—	—	Text Exact Reported	4 · Electrical properties · Figure 5b
electrical conductivity at 300 K	6 x 10^-8 S cm^-1	6e-8 S cm^-1	—	Text Exact Reported	4 · Electrical properties · Figure 5a
electrical conductivity at 400 K	5.4 x 10^-6 S cm^-1	0.0000054 S cm^-1	—	Text Exact Reported	4 · Electrical properties · Figure 5a

Fe-THBQ pressed cuboid pellet · Pellet

Pressed cuboid pellet measured with KEITHLEY 2002 multimeter; temperature range 300-400 K.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
activation energy from Arrhenius conductivityMarked as a best value within this paper	0.23 eV	—	—	Text Exact Reported	4 · Electrical properties · Figure 5b
electrical conductivity at 300 KMarked as a best value within this paper	2.7 x 10^-4 S cm^-1	0.00027 S cm^-1	—	Text Exact Reported	4 · Electrical properties · Figure 5a
electrical conductivity at 400 K	2.7 x 10^-3 S cm^-1	0.0027 S cm^-1	—	Text Exact Reported	4 · Electrical properties · Figure 5a

Mn-THBQ pressed cuboid pellet · Pellet

Pressed cuboid pellet measured with KEITHLEY 2002 multimeter; temperature range 300-400 K.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
activation energy from Arrhenius conductivity	0.48 eV	—	—	Text Exact Reported	4 · Electrical properties · Figure 5b
electrical conductivity at 300 K	3.5 x 10^-8 S cm^-1	3.5e-8 S cm^-1	—	Text Exact Reported	4 · Electrical properties · Figure 5a
electrical conductivity at 400 K	3.7 x 10^-6 S cm^-1	0.0000037 S cm^-1	—	Text Exact Reported	4 · Electrical properties · Figure 5a