Three-Dimensional-Coordination Polymer of Zn(II)-Carboxylate: Structural Elucidation, Photoelectrical Conductivity, and Biological Activity · Chandra A., Das M., Pal K. et al. · ACS Omega · 2019 · 17649-17661
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
compound 1 thin-film Schottky diode · Thin Film
Conductivity measured from the slope of resultant I-V graph; normal temperature and ambient conditions.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| electrical conductivityMarked as a best value within this paper | 1.37 x 10^-6 S/cm | 0.000137 S/m | — | Text Exact Reported | 17652 · Results and Discussion, I-V Measurement and Analysis |
compound 1 thin-film Schottky diode · Thin Film
ITO/compound 1/Al device; voltage range -1 to +1 V; dark and light conditions; normal temperature and ambient conditions.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Schottky barrier height under dark | 0.60 eV | — | — | Table Exact Reported | 17653-17654 · Results and Discussion, I-V Measurement and Analysis · Table 1 |
| Schottky barrier height under lightMarked as a best value within this paper | 0.58 eV | — | — | Table Exact Reported | 17654 · Results and Discussion, I-V Measurement and Analysis · Table 1 |
| specific detectivity D*Marked as a best value within this paper | 2.17 x 10^10 Jones | — | — | Table Exact Reported | 17653 · Results and Discussion, I-V Measurement and Analysis · Table 1 |
| ideality factor n under dark | 3.41 | — | — | Table Exact Reported | 17653 · Results and Discussion, I-V Measurement and Analysis · Table 1 |
| ideality factor n under lightMarked as a best value within this paper | 2.91 | — | — | Table Exact Reported | 17653 · Results and Discussion, I-V Measurement and Analysis · Table 1 |
| on/off ratio under dark | 93 | — | — | Table Exact Reported | 17653 · Results and Discussion, I-V Measurement and Analysis · Table 1 |
| on/off ratio under lightMarked as a best value within this paper | 129 | — | — | Table Exact Reported | 17653 · Results and Discussion, I-V Measurement and Analysis · Table 1 |
| photosensitivity SMarked as a best value within this paper | 20.95 | — | — | Table Exact Reported | 17653 · Results and Discussion, I-V Measurement and Analysis · Table 1 |
| responsivity RMarked as a best value within this paper | 56.21 mA/W | 0.05621 A/W | — | Table Exact Reported | 17653 · Results and Discussion, I-V Measurement and Analysis · Table 1 |
| series resistance from dV/dln(I), dark | 1.37 x 10^6 | — | — | Table Exact Reported | 17653 · Results and Discussion, I-V Measurement and Analysis · Table 1 |
| series resistance from dV/dln(I), lightMarked as a best value within this paper | 6.56 x 10^5 | — | — | Table Exact Reported | 17653 · Results and Discussion, I-V Measurement and Analysis · Table 1 |
compound 1 thin-film Schottky diode · Thin Film
Frequency 40 Hz to 11 MHz using Agilent 4294A LCR meter; compound 1 and ppmh devices compared.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Nyquist semicircle diameter for compound 1 deviceMarked as a best value within this paper | approximately 1.2 x 10^5 ohm from Figure 10/S4 x-axis intercept | — | visual estimate from plotted axis | Figure Axis Approximate | S3 · Supporting Information · Figure S4 |
| Nyquist semicircle diameter for ppmh device | approximately 6.2 x 10^5 ohm from Figure 10 x-axis intercept | — | visual estimate from plotted axis | Figure Axis Approximate | 17654 · Results and Discussion, I-V Measurement and Analysis · Figure 10 |
ppmh ligand thin-film Schottky diode · Thin Film
Conductivity measured from the slope of resultant I-V graph; normal temperature and ambient conditions.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| electrical conductivity | 6.2 x 10^-7 S/cm | 0.000062 S/m | — | Text Exact Reported | 17652 · Results and Discussion, I-V Measurement and Analysis |
ppmh ligand thin-film Schottky diode · Thin Film
ppmh-based SBD; voltage range -1 to +1 V; dark and light conditions.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Schottky barrier height under dark | 0.65 eV | — | — | Table Exact Reported | 17654 · Results and Discussion, I-V Measurement and Analysis · Table 1 |
| Schottky barrier height under light | 0.61 eV | — | — | Table Exact Reported | 17654 · Results and Discussion, I-V Measurement and Analysis · Table 1 |
| specific detectivity D* | 4.53 x 10^9 Jones | — | — | Table Exact Reported | 17653 · Results and Discussion, I-V Measurement and Analysis · Table 1 |
| ideality factor n under dark | 4.26 | — | — | Table Exact Reported | 17653 · Results and Discussion, I-V Measurement and Analysis · Table 1 |
| ideality factor n under light | 3.87 | — | — | Table Exact Reported | 17653 · Results and Discussion, I-V Measurement and Analysis · Table 1 |
| on/off ratio under dark | 32 | — | — | Table Exact Reported | 17653 · Results and Discussion, I-V Measurement and Analysis · Table 1 |
| on/off ratio under light | 65 | — | — | Table Exact Reported | 17653 · Results and Discussion, I-V Measurement and Analysis · Table 1 |
| photosensitivity S | 9.98 | — | — | Table Exact Reported | 17653 · Results and Discussion, I-V Measurement and Analysis · Table 1 |
| responsivity R | 5.12 mA/W | 0.00512 A/W | — | Table Exact Reported | 17653 · Results and Discussion, I-V Measurement and Analysis · Table 1 |
| series resistance from dV/dln(I), dark | 7.71 x 10^7 | — | — | Table Exact Reported | 17653 · Results and Discussion, I-V Measurement and Analysis · Table 1 |
| series resistance from dV/dln(I), light | 7.11 x 10^6 | — | — | Table Exact Reported | 17653 · Results and Discussion, I-V Measurement and Analysis · Table 1 |
compound 1 thin-film Schottky diode · Thin Film
1.5 G illumination, 100 mW/cm2; light switched on and off at 60 s intervals for 600 s.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| transient photocurrent response behaviour | steady and reproducible rectangular on-off photoresponse; better response speed for compound 1 than ppmh | — | — | Text Qualitative | 17652 · Results and Discussion, I-V Measurement and Analysis · Figure 8 |