Porosity — Is iron unique in promoting electrical conductivity in MOFs?

4 measurement groups · 4 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

pressed pellet of Fe2Cl2(BTDD)(DMF)2 · Pellet

Sample heated to 100 deg C until outgas rate less than 2 mtorr/min; N2 adsorption measured at 77 K.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface area	365 m2/g	—	—	SI Table Exact Reported	S46 · Table S3 · Table S3

pressed pellet of Fe2(DOBDC)(DMF)2 · Pellet

Sample heated to 100 deg C until outgas rate less than 2 mtorr/min; N2 adsorption measured at 77 K.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface area	248 m2/g	—	—	SI Table Exact Reported	S46 · Table S3 · Table S3

pressed pellet of Fe2(DSBDC)(DMF)2 · Pellet

Sample heated to 100 deg C until outgas rate less than 2 mtorr/min; N2 adsorption measured at 77 K.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface area	83 m2/g	—	—	SI Table Exact Reported	S46 · Table S3 · Table S3

pressed pellet of Fe(1,2,3-triazolate)2 · Pellet

Sample heated to 100 deg C until outgas rate less than 2 mtorr/min; N2 adsorption measured at 77 K.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface areaMarked as a best value within this paper	443 m2/g	—	—	SI Table Exact Reported	S46 · Table S3 · Table S3