Porosity — Shielding against Unfolding by Embedding Enzymes in Metal-Organic Frameworks via a de Novo Approach

2 measurement groups · 8 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

CAT@ZIF-90 · Powder

Samples degassed at 110 deg C for 12 h before measurement; P/P0 = 0.06-0.20 used for surface-area calculation.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface area	918 m2 g-1	—	—	SI Table Exact Reported	S17 · Table Section · Table S2
Langmuir surface area	1212 m2 g-1	—	—	SI Table Exact Reported	S17 · Table Section · Table S2
T-plot micropore volume	0.40 cm3 g-1	—	—	SI Table Exact Reported	S17 · Table Section · Table S2
Total pore volume	0.52 cm3 g-1	—	—	SI Table Exact Reported	S17 · Table Section · Table S2

ZIF-90 microcrystals · Powder

Samples degassed at 110 deg C for 12 h before measurement; P/P0 = 0.06-0.20 used for surface-area calculation.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface area	1068 m2 g-1	—	—	SI Table Exact Reported	S17 · Table Section · Table S2
Langmuir surface area	1410 m2 g-1	—	—	SI Table Exact Reported	S17 · Table Section · Table S2
T-plot micropore volume	0.46 cm3 g-1	—	—	SI Table Exact Reported	S17 · Table Section · Table S2
Total pore volume	0.63 cm3 g-1	—	—	SI Table Exact Reported	S17 · Table Section · Table S2