cMOF Evidence Base
Electrical Transport — A chiral SrSi2 (srs) superstructure constructed by a dual interaction system showing isotropic electrical conductivity

Measurement evidence

Electrical Transport

A chiral SrSi2 (srs) superstructure constructed by a dual interaction system showing isotropic electrical conductivity · Liu J., Lu Z.-X., Wu F.-F. et al. · Chinese Chemical Letters · 2023 · 108100

2 measurement groups · 8 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Two-probe electrical conductivity measurement

Electrical conductivity

Pellet of compound 1 · Pellet

Keithley 2400 parameter analyser; pellet of compound 1 measured at 300 K; voltage swept from -5 V to +5 V.

Temperature
300
Geometry
3-mm pellet; silver glue contacts; 50 micrometre gold wire; two-probe
Context
pristine framework pellet
Measurement source
SI office text · Electrical conductivity measurement · Fig. 3a
PropertyReported valueNormalised valueUncertaintyOrigin and qualitySource
Electrical conductivityMarked as a best value within this paper2.01 x 10^-7 S/cm at 300 K0.0000201 S/m—Text
Exact Reported		main p.3 · Main text · Fig. 3a
Electrical conductivity rounded in abstract2.1 x 10^-7 S/cm0.000021 S/m—Text
Rounded Reported		main p.1 · Abstract
Approximate current at +5 V from I-V plotabout +0.37 microampere at +5 V3.7e-7 Avisual estimate from plotted axisFigure Axis
Approximate		main p.3 · Figure plot · Fig. 3a
I-V responseapproximately linear current-voltage curve at room temperature——Figure Axis
Qualitative		main p.3 · Figure plot · Fig. 3a
I-V voltage sweep range-5 V to +5 V——Text
Range		SI office text · Electrical conductivity measurement
Directionality label in Table S2isotropic——SI Table
Qualitative		SI rendered p.5 · Comparison of electrical conductivities of selected conductive MOFs and 1 · Table S2
Table S2 conductivity comparison entry for compound 1[AgI3L2].3OTf: 2.1 x 10^-7 S/cm; isotropic; This work0.000021 S/m—SI Table
Rounded Reported		SI rendered p.5 · Comparison of electrical conductivities of selected conductive MOFs and 1 · Table S2

Two-probe I-V/electrical conductivity measurement on regenerated compound 1

Electrical conductivity

Regenerated compound 1 crystals · Single Crystal

SI Fig. S7 caption reports room-temperature I-V curve and regenerated conductivity.

Geometry
not specified; comparable to as-synthesised pellet measurement
Context
regenerated pristine framework
Measurement source
SI office text · I-V curve and UV-vis-NIR spectrum of regenerated 1 · Fig. S7
PropertyReported valueNormalised valueUncertaintyOrigin and qualitySource
Electrical conductivity of regenerated compound 11.86 x 10^-7 S/cm0.0000186 S/m—Caption
Exact Reported		SI office text · I-V curve and UV-vis-NIR spectrum of regenerated 1 · Fig. S7