Porosity — Soft Electrochemical Actuators with a Two-Dimensional Conductive Metal-Organic Framework Nanowire Array

Measurement evidence

Porosity

Soft Electrochemical Actuators with a Two-Dimensional Conductive Metal-Organic Framework Nanowire Array · Shi Y.-X., Wu Y., Wang S.-Q. et al. · Journal of the American Chemical Society · 2021 · 4017-4023

1 measurement group · 2 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

N2 adsorption/desorption and BET/BJH analysis

Gas sorption and porosity

core-shell Ni-CAT NWAs/CNF electrode · Electrode

N2 sorption at 77 K after degassing at 100 C under vacuum (10^-5 mbar) for 12 h; BET surface area and BJH pore distribution.

Temperature: 77
Atmosphere: N2 adsorption; vacuum degas before measurement
Context: Activated Ni-CAT NWAs/CNF composite.
Measurement source: p004-p005 / SI p.S1-S2 · Characterization · Figure 2b; Figure S6

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface area of Ni-CAT NWAs/CNFMarked as a best value within this paper	371 m2 g^-1	—	—	Text Exact Reported	p003 / article p.4019 · Synthesis and Characterization · Figure S6; Table S1
N2 isotherm type	Type I isotherm profiles indicate microporous nature	—	—	Text Qualitative	p003 / article p.4019 · Synthesis and Characterization · Figure 2b