Other — Turning 2D MOFs into Mixed Ionic-Electronic Conductors via Side Chain Engineering

6 measurement groups · 12 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Ni-1EG pristine powder · Powder

cluster sizes in acetone and water

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
DLS cluster size in acetoneMarked as a best value within this paper	~20 nm	—	—	Text Approximate	p006 · Results and Discussion · Figure S33
DLS larger cluster size in water	~200 nm	—	—	Text Approximate	p006 · Results and Discussion · Figure S33
DLS small cluster size in waterMarked as a best value within this paper	~3.5 nm	—	—	Text Approximate	p006 · Results and Discussion · Figure S33

Ni-2EG pristine powder · Powder

cluster sizes in acetone and water

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
DLS cluster size in acetone	~150 nm	—	—	Text Approximate	p006 · Results and Discussion · Figure S33
DLS larger cluster size in water	~600 nm	—	—	Text Approximate	p006 · Results and Discussion · Figure S33
DLS small cluster size in water	~20 nm	—	—	Text Approximate	p006 · Results and Discussion · Figure S33

Ni-nBu pristine powder · Powder

cluster sizes in acetone and water

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
DLS cluster size in acetone	~420 nm	—	—	Text Approximate	p006 · Results and Discussion · Figure S33
DLS larger cluster size in water	~1000 nm	—	—	Text Approximate	p006 · Results and Discussion · Figure S33
DLS small cluster size in water	~250 nm	—	—	Text Approximate	p006 · Results and Discussion · Figure S33

LiTFSI-Ni-1EG · Powder

Li/Ni molar ratio after 3 days in 1 M LiTFSI/PC

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Li/Ni molar ratio after LiTFSI soakingMarked as a best value within this paper	0.12069	—	—	Text Exact Reported	p004 · Results and Discussion · Figure 3c

LiTFSI-Ni-2EG · Powder

Li/Ni molar ratio after 3 days in 1 M LiTFSI/PC

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Li/Ni molar ratio after LiTFSI soaking	0.04978	—	—	Text Exact Reported	p004 · Results and Discussion · Figure 3c

LiTFSI-Ni-nBu · Powder

Li/Ni molar ratio after 3 days in 1 M LiTFSI/PC

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Li/Ni molar ratio after LiTFSI soaking	0.10679	—	—	Text Exact Reported	p004 · Results and Discussion · Figure 3c