Microscopy Morphology — Enhancing electrochemical hydrogen storage in nickel-based metal-organic frameworks (MOFs) through zinc and cobalt doping as bimetallic MOFs

4 measurement groups · 10 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Co-Ni(TPA)-2 · Powder

EDX spectrum and elemental mapping for Co-Ni(TPA)-2.

Geometry: powder
Context: Co-doped Ni(TPA)
Measurement source: 350 · 3.1. Characterization of synthesized MOFs · Figs. 3 and 4

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Co atomic content by EDX	Co At (%) = 5.89	—	—	Visual Estimate Rounded Reported	352 · Figure page · Fig. 3 inset table
Co/Ni ratio	Co/Ni ratio = 0.78	—	—	Text Rounded Reported	350 · 3.1. Characterization of synthesized MOFs · Fig. 3
Co content by EDX	Co Wt (%) = 17.25	—	—	Visual Estimate Rounded Reported	352 · Figure page · Fig. 3 inset table
Ni atomic content by EDX	Ni At (%) = 7.54	—	—	Visual Estimate Rounded Reported	352 · Figure page · Fig. 3 inset table
Ni content by EDX	Ni Wt (%) = 22.19	—	—	Visual Estimate Rounded Reported	352 · Figure page · Fig. 3 inset table

Co-Ni(TPA)-2 · Powder

Low and high magnification SEM images.

Geometry: powder
Context: Co-doped Ni(TPA)
Measurement source: 351 · 3.1. Characterization of synthesized MOFs · Fig. 2e,f

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Morphology	regular petal-like sheets	—	—	Text Qualitative	350 · 3.1. Characterization of synthesized MOFs · Fig. 2e,f

Ni(TPA) · Powder

Low and high magnification SEM images.

Geometry: powder
Context: pristine Ni(TPA)
Measurement source: 351 · 3.1. Characterization of synthesized MOFs · Fig. 2a,b

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Morphology	significant number of nanosheets	—	—	Text Qualitative	350 · 3.1. Characterization of synthesized MOFs · Fig. 2a

Zn-Ni(TPA)-2 · Powder

Low and high magnification SEM images.

Geometry: powder
Context: Zn-doped Ni(TPA)
Measurement source: 351 · 3.1. Characterization of synthesized MOFs · Fig. 2c,d

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Average distance between adjacent nanosheets in bimetallic samples	about 45 nm	—	—	Text Approximate	350 · 3.1. Characterization of synthesized MOFs · Fig. 2
Average sheet thickness in bimetallic samples	about 22 nm	—	—	Text Approximate	350 · 3.1. Characterization of synthesized MOFs · Fig. 2
Morphology	regular petal-like sheets	—	—	Text Qualitative	350 · 3.1. Characterization of synthesized MOFs · Fig. 2c,d