Other — Defect Engineering to Tailor Metal Vacancies in 2D Conductive Metal-Organic Frameworks: An Example in Electrochemical Sensing

3 measurement groups · 9 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Ag-BHT film prepared at pH 2 · Thin Film

Elemental concentrations for Ag-BHT films prepared at pH 2, 1, and 0.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Ag-BHT pH 0 Ag content	Ag 61.2 wt%	—	—	SI Table Exact Reported	30 · 2.3 Supplemental Data · Table S3
Ag-BHT pH 2 Ag content	Ag 43.7 wt%	—	—	SI Table Exact Reported	30 · 2.3 Supplemental Data · Table S3

Cu-BHT film prepared at pH 2 · Thin Film

Elemental concentrations for Cu-BHT films prepared at pH 2, 1, and 0.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Cu-BHT pH 0 Cu content	Cu 41.1 wt%	—	—	SI Table Exact Reported	20 · 2.3 Supplemental Data · Table S1
Cu-BHT pH 1 Cu content	Cu 36.9 wt%	—	—	SI Table Exact Reported	20 · 2.3 Supplemental Data · Table S1
Cu-BHT pH 2 C content	C 20.4 wt%	—	—	SI Table Exact Reported	20 · 2.3 Supplemental Data · Table S1
Cu-BHT pH 2 Cu content	Cu 26.8 wt%	—	—	SI Table Exact Reported	20 · 2.3 Supplemental Data · Table S1
Cu-BHT pH 2 S content	S 52.8 wt%	—	—	SI Table Exact Reported	20 · 2.3 Supplemental Data · Table S1

Ni-BHT film prepared at pH 2 · Thin Film

Elemental concentrations for Ni-BHT films prepared at pH 2, 1, and 0.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Ni-BHT pH 0 Ni content	Ni 24.6 wt%	—	—	SI Table Exact Reported	29 · 2.3 Supplemental Data · Table S2
Ni-BHT pH 2 Ni content	Ni 20.8 wt%	—	—	SI Table Exact Reported	29 · 2.3 Supplemental Data · Table S2