Microscopy Morphology — In-Built Fabrication of MOF Assimilated Porous Hollow Carbon from Pre-Hydrolysate for Supercapacitor

5 measurement groups · 5 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

C1-ZIF-67 powder · Powder

JSM-7401F SEM at 20 kV.

Context: one-step ZIF-67/carbon composite
Measurement source: p005 / article p.5 · 3 Results and Discussion · Figure 2c,e

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
SEM particle size	0.1 um	—	—	Text Rounded Reported	p005 / article p.5 · 3 Results and Discussion · Figure 2c,e

C2-ZIF-67 powder · Powder

JSM-7401F SEM at 20 kV.

Context: two-step target ZIF-67/carbon composite
Measurement source: p005-p006 / article pp.5-6 · 3 Results and Discussion · Figure 2d,f

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
SEM particle size	0.35-0.90 um	—	range	Text Range	p005 / article p.5 · 3 Results and Discussion · Figure 2d,f

Carbon-hydrolysate powder · Powder

JSM-7401F SEM at 20 kV.

Context: pristine carbon comparison
Measurement source: p003-p005 / article pp.3-5 · 2.2 Characterization; 3 Results and Discussion · Figure 2a

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
SEM particle size	1-2 um smooth spheres	—	range	Text Range	p005 / article p.5 · 3 Results and Discussion · Figure 2a

Co-MOF (ZIF-67) purple powder · Powder

JSM-7401F SEM at 20 kV.

Context: pristine Co-MOF control
Measurement source: p005 / article p.5 · 3 Results and Discussion · Figure 2b

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
SEM particle size	0.3-0.8 um	—	range	Text Range	p005 / article p.5 · 3 Results and Discussion · Figure 2b

C2-ZIF-67 powder · Powder

JEOL 2011 TEM at 200 kV.

Context: two-step target composite
Measurement source: p006-p007 / article pp.6-7 · 3 Results and Discussion · Figure 3d-f

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Hollow interiorMarked as a best value within this paper	C2-ZIF-67 exhibited a hollow structure	—	—	Text Qualitative	p007 / article p.7 · 3 Results and Discussion · Figure 3e,f