Microscopy Morphology — Li + Ion-Conducting Sulfonate-Based Neutral Metal-Organic Framework

Measurement evidence

Microscopy Morphology

Li + Ion-Conducting Sulfonate-Based Neutral Metal-Organic Framework · Panda D.K., Maity K., Palukoshka A. et al. · ACS Sustainable Chemistry and Engineering · 2019 · 4619-4624

1 measurement group · 2 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

SEM-EDX

Scanning electron microscopyElemental microanalysis and mapping

LiClO4-treated Cu(I)-sulfonate MOF pellet · Pellet

SEM-EDX comparison of pristine and LiClO4-treated Cu(I)-sulfonate MOF.

Geometry
MOF films on FTO per SI method; figure reports pristine top and LiClO4-treated bottom.
Context
Pristine and LiClO4-treated comparison.
Measurement source
SI p.S-6 · Figure S3 · Figure S3
PropertyReported valueNormalised valueUncertaintyOrigin and qualitySource
Cl content in LiClO4-treated MOF by EDXCl K 5.97 wt%, 2.57 atomic%——Figure Axis
Exact Reported		SI p.S-6 · Figure S3 · Figure S3 bottom EDX table
Cu content in pristine MOF by EDXCu L 9.78 wt%, 2.30 atomic%——Figure Axis
Exact Reported		SI p.S-6 · Figure S3 · Figure S3 top EDX table