cMOF Evidence Base
Porosity — Li + Ion-Conducting Sulfonate-Based Neutral Metal-Organic Framework

Measurement evidence

Porosity

Li + Ion-Conducting Sulfonate-Based Neutral Metal-Organic Framework · Panda D.K., Maity K., Palukoshka A. et al. · ACS Sustainable Chemistry and Engineering · 2019 · 4619-4624

1 measurement group · 1 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

N2 sorption isotherm and BET surface-area analysis

Gas sorption and porosity

Activated pristine [Cu2(BPY)2(NDIDS)] MOF powder · Powder

Activated MOF measured by Quantachrome Autosorb iQ Gas Sorption Analyzer; isotherm at 300 K.

Temperature
300
Atmosphere
N2
Geometry
powder, 99 mg activated MOF in SI method
Context
Activated pristine framework.
Measurement source
main p.3, article p.4621 · Results and Discussion · Figure S2
PropertyReported valueNormalised valueUncertaintyOrigin and qualitySource
BET surface areaMarked as a best value within this paper~20 m2/g——Text
Approximate		main p.3, article p.4621 · Results and Discussion · Figure S2