Other — Dimensional Control of Highly Anisotropic and Transparent Conductive Coordination Polymers for Solution-Processable Large-Scale 2D Sheets

Measurement evidence

Other

Dimensional Control of Highly Anisotropic and Transparent Conductive Coordination Polymers for Solution-Processable Large-Scale 2D Sheets · Suh B.L., Kang G., Yoon S.M. et al. · Advanced Materials · 2023 · 2206980

1 measurement group · 3 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Temperature-dependent XRD and TG/DTG

X-ray diffraction and scattering Thermogravimetric analysis

1D CuCl-TU polymer nanowire · Powder

Heat treatment XRD and thermogravimetry of CuCl-TU polymers/nanowires.

Atmosphere: airflow 30 mL/min for TG/DTG
Context: pristine framework
Measurement source: 7 · Results and Discussion · Figures S33-S34

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Absorbed-water evaporation range	100-200 C	—	—	Text Range	7 · Results and Discussion · Figure S34
Different material after heating	fully different materials were obtained after heat treatment above 200 C	—	—	Text Approximate	7 · Results and Discussion · Figure S33
Thermal XRD change onset	peak intensities change above 100 C	—	—	Text Approximate	7 · Results and Discussion · Figure S33