Electrochemical Transformation of Metal Organic Framework into Ultrathin Metal Hydroxide-(oxy)hydroxide Nanosheets for Alkaline Water Oxidation · Singh B., Prakash O., Maiti P. et al. · ACS Applied Nano Materials · 2020 · 6693-6701
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
CF-2 · Electrode
Oxidation state and Fe leaching analysis of ultrathin CF-2 nanosheets
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| CF-2 Co 2p spin-orbit spacing | 15.2 eV | — | — | Caption Exact Reported | 6696 · 3.2 · Figure 2a |
| Fe leached from CoFe-PBA to form CF-2 | 92% of Fe was leached out | — | — | Text Exact Reported | 6696 · 3.2 |
| Fe content in CF catalyst systems | 5-8% | — | range 5-8 | Text Range | 6696 · 3.2 |
CoFe-PBA@CC · Electrode
Thermo Scientific Nicolet iS5 spectrometer with ATR mode
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| bridged CN FTIR peak | 2130 cm-1 | — | — | Caption Exact Reported | S-6 · 6. Figures · Figure S2 |
| bridged CN FTIR peak | 2170 cm-1 | — | — | Caption Exact Reported | S-6 · 6. Figures · Figure S2 |
CoFe-PBA@CC · Electrode
VG/VG ESCA LAB 220i; Co 2p, Fe 2p, O 1s, C 1s, N 1s
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Co 2p spin-orbit spacing | 15.8 eV | — | — | Caption Exact Reported | S-8 · 6. Figures · Figure S6 |
| Fe 2p3/2 binding energy | 708.3 eV | — | — | Caption Exact Reported | S-8 · 6. Figures · Figure S7 |