Porosity — Synergistic Enhancement of Supercapacitors with Cobalt–Copper Bimetal–Organic Framework

Measurement evidence

Porosity

Synergistic Enhancement of Supercapacitors with Cobalt–Copper Bimetal–Organic Framework · Zhang Z., Wang Z., Dong M. et al. · Advanced Engineering Materials · 2024 · 2400378

3 measurement groups · 14 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

N2 sorption BET and XRF

Bulk elemental and compositional analysisGas sorption and porosity

Co-MOF powder · Powder

Nitrogen adsorption-desorption on Micromeritics ASAP 2020 HD 88; XRF for Cu/Co contents

Atmosphere
N2
Context
pristine powder
Measurement source
3 · Results and Discussion · Table 1
PropertyReported valueNormalised valueUncertaintyOrigin and qualitySource
average pore diameter14.8 nm——Table
Exact Reported		3 · Results and Discussion · Table 1
total pore volume0.10 cm3 g-1——Table
Exact Reported		3 · Results and Discussion · Table 1
BET specific surface area24.3 m2 g-1——Table
Exact Reported		3 · Results and Discussion · Table 1
XRF Co content19.6 wt%——Table
Exact Reported		3 · Results and Discussion · Table 1

N2 sorption BET and XRF

Bulk elemental and compositional analysisGas sorption and porosity

CoCu-MOF powder, Co:Cu = 6:1 feed · Powder

Nitrogen adsorption-desorption on Micromeritics ASAP 2020 HD 88; XRF for Cu/Co contents

Atmosphere
N2
Context
pristine powder
Measurement source
3 · Results and Discussion · Table 1
PropertyReported valueNormalised valueUncertaintyOrigin and qualitySource
average pore diameter18.7 nm——Table
Exact Reported		3 · Results and Discussion · Table 1
total pore volume0.14 cm3 g-1——Table
Exact Reported		3 · Results and Discussion · Table 1
BET specific surface area62.4 m2 g-1——Table
Exact Reported		3 · Results and Discussion · Table 1
XRF Co:Cu atom ratio6.2——Table
Exact Reported		3 · Results and Discussion · Table 1
XRF Co content18.1 wt%——Table
Exact Reported		3 · Results and Discussion · Table 1
XRF Cu content3.1 wt%——Table
Exact Reported		3 · Results and Discussion · Table 1

N2 sorption BET and XRF

Bulk elemental and compositional analysisGas sorption and porosity

Cu-MOF powder · Powder

Nitrogen adsorption-desorption on Micromeritics ASAP 2020 HD 88; XRF for Cu/Co contents

Atmosphere
N2
Context
pristine powder
Measurement source
3 · Results and Discussion · Table 1
PropertyReported valueNormalised valueUncertaintyOrigin and qualitySource
average pore diameterMarked as a best value within this paper28.0 nm——Table
Exact Reported		3 · Results and Discussion · Table 1
total pore volumeMarked as a best value within this paper0.33 cm3 g-1——Table
Exact Reported		3 · Results and Discussion · Table 1
BET specific surface areaMarked as a best value within this paper80.9 m2 g-1——Table
Exact Reported		3 · Results and Discussion · Table 1
XRF Cu content21.6 wt%——Table
Exact Reported		3 · Results and Discussion · Table 1