Measurement evidence
Tuning the Electrical Conductivity of Bimetallic Co–Mn-Based MOFs via Precisely Regulating the Atomic Content of Metal Centers and Study on Their Dye Adsorption Properties · Hazarika U.N., Sonowal K., Mostako A.T.T. et al. · Inorganic Chemistry · 2025 · 15748-15759
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
Guest-removed d-MOF1 · Powder
Guest-removed d-MOF pellet measured at 25 deg C under 60% humidity.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| d-MOF1 electrical conductivity at 25 deg CMarked as a best value within this paper | 6.02 S cm^-1 | — | — | Table Exact Reported | main p.7, article p.15754 · Results and discussion · Table 3 |
Guest-removed d-MOF2 · Powder
Guest-removed d-MOF pellet measured at 25 deg C under 60% humidity.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| d-MOF2 electrical conductivity at 25 deg C | 1.43 S cm^-1 | — | — | Table Exact Reported | main p.7, article p.15754 · Results and discussion · Table 3 |
Guest-removed d-MOF3 · Powder
Guest-removed d-MOF pellet measured at 25 deg C under 60% humidity.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| d-MOF3 electrical conductivity at 25 deg C | 0.75 S cm^-1 | — | — | Table Exact Reported | main p.7, article p.15754 · Results and discussion · Table 3 |
Guest-removed d-MOF4 · Powder
Guest-removed d-MOF pellet measured at 25 deg C under 60% humidity.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| d-MOF4 electrical conductivity at 25 deg C | 0.49 S cm^-1 | — | — | Table Exact Reported | main p.7, article p.15754 · Results and discussion · Table 3 |
Guest-removed d-MOF5 · Powder
Guest-removed d-MOF pellet measured at 25 deg C under 60% humidity.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| d-MOF5 electrical conductivity at 25 deg C | 5.83 S cm^-1 | — | — | Table Exact Reported | main p.7, article p.15754 · Results and discussion · Table 3 |
Guest-removed d-MOF6 · Powder
Guest-removed d-MOF pellet measured at 25 deg C under 60% humidity.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| d-MOF6 electrical conductivity at 25 deg C | 3.59 S cm^-1 | — | — | Table Exact Reported | main p.7, article p.15754 · Results and discussion · Table 3 |
Guest-removed d-MOF7 · Powder
Guest-removed d-MOF pellet measured at 25 deg C under 60% humidity.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| d-MOF7 electrical conductivity at 25 deg C | 0.82 S cm^-1 | — | — | Table Exact Reported | main p.7, article p.15754 · Results and discussion · Table 3 |
Guest-removed d-MOF8 · Powder
Guest-removed d-MOF pellet measured at 25 deg C under 60% humidity.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| d-MOF8 electrical conductivity at 25 deg C | 0.41 S cm^-1 | — | — | Table Exact Reported | main p.7, article p.15754 · Results and discussion · Table 3 |
Guest-removed d-MOF9 · Powder
Guest-removed d-MOF pellet measured at 25 deg C under 60% humidity.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| d-MOF9 electrical conductivity at 25 deg C | 0.15 S cm^-1 | — | — | Table Exact Reported | main p.7, article p.15754 · Results and discussion · Table 3 |
As-synthesised MOF1-MOF9 bulk series · Powder
I-V curves for MOF1-MOF9 recorded at 25 deg C under 60% humidity.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| ohmic response | linear current response to applied potential; MOFs are ohmic materials | — | — | Text Qualitative | main p.5, article p.15752 · Results and discussion · Figure 5 |
As-synthesised MOF1-MOF9 bulk series · Powder
9 V battery, 4-band current-limiting resistor, LED, and MOF pellet integrated in circuit.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| LED illumination through MOF pellet | LED illuminated after integrating a MOF pellet | — | — | Text Qualitative | main p.7, article p.15754 · Results and discussion · Figure 11 |
As-synthesised MOF1 · Powder
Keithley 2450 source meter; pellets 1.3 cm diameter and 2 mm thick; 25 deg C under 60% humidity.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| MOF1 electrical conductivity at 25 deg CMarked as a best value within this paper | 19.73 S cm^-1 | — | — | Table Exact Reported | main p.5, article p.15752 · Results and discussion · Table 1 |
As-synthesised MOF1 · Powder
Representative I-V measurements at 30, 40 and 50 deg C; activation energy tabulated.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| MOF1 activation energy for charge mobility | 0.0203 eV | — | — | Table Exact Reported | main p.6, article p.15753 · Results and discussion · Table 2 |
| MOF1 temperature trend | conductivity decreases with increase in temperature, indicating metallic nature | — | — | Text Qualitative | main p.5-6, article p.15752-15753 · Results and discussion · Figure 7 |
As-synthesised MOF2 · Powder
Keithley 2450 source meter; pellets 1.3 cm diameter and 2 mm thick; 25 deg C under 60% humidity.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| MOF2 electrical conductivity at 25 deg C | 3.75 S cm^-1 | — | — | Table Exact Reported | main p.5, article p.15752 · Results and discussion · Table 1 |
As-synthesised MOF3 · Powder
Keithley 2450 source meter; pellets 1.3 cm diameter and 2 mm thick; 25 deg C under 60% humidity.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| MOF3 electrical conductivity at 25 deg C | 1.14 S cm^-1 | — | — | Table Exact Reported | main p.5, article p.15752 · Results and discussion · Table 1 |
As-synthesised MOF3 · Powder
Representative I-V measurements at 30, 40 and 50 deg C; activation energy tabulated.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| MOF3 activation energy for charge mobility | 0.0179 eV | — | — | Table Exact Reported | main p.6, article p.15753 · Results and discussion · Table 2 |
| MOF3 temperature trend | conductivity decreases with increase in temperature, indicating metallic nature | — | — | Text Qualitative | main p.5-6, article p.15752-15753 · Results and discussion · Figure 7 |
As-synthesised MOF4 · Powder
Keithley 2450 source meter; pellets 1.3 cm diameter and 2 mm thick; 25 deg C under 60% humidity.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| MOF4 electrical conductivity at 25 deg C | 0.08 S cm^-1 | — | — | Table Exact Reported | main p.5, article p.15752 · Results and discussion · Table 1 |
As-synthesised MOF5 · Powder
Keithley 2450 source meter; pellets 1.3 cm diameter and 2 mm thick; 25 deg C under 60% humidity.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| MOF5 electrical conductivity at 25 deg C | 18.72 S cm^-1 | — | — | Table Exact Reported | main p.5, article p.15752 · Results and discussion · Table 1 |
As-synthesised MOF6 · Powder
Keithley 2450 source meter; pellets 1.3 cm diameter and 2 mm thick; 25 deg C under 60% humidity.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| MOF6 electrical conductivity at 25 deg C | 5.96 S cm^-1 | — | — | Table Exact Reported | main p.5, article p.15752 · Results and discussion · Table 1 |
As-synthesised MOF7 · Powder
Keithley 2450 source meter; pellets 1.3 cm diameter and 2 mm thick; 25 deg C under 60% humidity.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| MOF7 electrical conductivity at 25 deg C | 4.7 S cm^-1 | — | — | Table Exact Reported | main p.5, article p.15752 · Results and discussion · Table 1 |
As-synthesised MOF8 · Powder
Keithley 2450 source meter; pellets 1.3 cm diameter and 2 mm thick; 25 deg C under 60% humidity.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| MOF8 electrical conductivity at 25 deg C | 3.26 S cm^-1 | — | — | Table Exact Reported | main p.5, article p.15752 · Results and discussion · Table 1 |
As-synthesised MOF8 · Powder
Representative I-V measurements at 30, 40 and 50 deg C; activation energy tabulated.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| MOF8 activation energy for charge mobility | 0.0192 eV | — | — | Table Exact Reported | main p.6, article p.15753 · Results and discussion · Table 2 |
| MOF8 temperature trend | conductivity decreases with increase in temperature, indicating metallic nature | — | — | Text Qualitative | main p.5-6, article p.15752-15753 · Results and discussion · Figure 7 |
As-synthesised MOF9 · Powder
Keithley 2450 source meter; pellets 1.3 cm diameter and 2 mm thick; 25 deg C under 60% humidity.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| MOF9 electrical conductivity at 25 deg C | 0.34 S cm^-1 | — | — | Table Exact Reported | main p.5, article p.15752 · Results and discussion · Table 1 |