Diffraction Structure — Intrinsically Conductive π-d Conjugated Layers with Co–N4 Active Sites for Efficient Nitrate Electrocatalysis and Zinc-Nitrate Batteries

Measurement evidence

Diffraction Structure

Intrinsically Conductive π-d Conjugated Layers with Co–N4 Active Sites for Efficient Nitrate Electrocatalysis and Zinc-Nitrate Batteries · Namvar S., Arzani M., Sarkar A.M. et al. · ACS Applied Materials and Interfaces · 2026 · 24433-24443

1 measurement group · 1 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Powder X-ray diffraction (PXRD)

X-ray diffraction and scattering

Co3(HITP)2 powder · Powder

PXRD pattern measured over 2theta = 10-70 deg.

Geometry: Powder diffraction
Context: pristine Co3(HITP)2 powder
Measurement source: p.24435 · Results and Discussion · Figure S2

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
PXRD absence of discernible diffraction peaks	No discernible diffraction peaks within 2theta 10-70 deg	—	2theta 10-70 deg range	Text Qualitative	p.24435 · Results and Discussion · Figure S2