Measurement evidence
Iodine uptake enhanced electrical conductivity by a metal-organic framework bearing nanotube array of π-stacked columns · Chen T., Li S., Wang Z.-B. et al. · Journal of Molecular Structure · 2023 · 135858
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
compound 1 pellet · Pellet
Pressed pellet; silver glue contacts; 50 um gold wire; I-V sweep from 0 to +1 V; measured at 300 K
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| electrical conductivity of compound 1 | 1.86 x 10^-13 S cm^-1 | 1.86e-11 S m^-1 | — | Text Exact Reported | 5 · 3.5. Guest tunable electric conductivities · Fig. 5; Fig. S10 |
desolvated 1 pellet · Pellet
Pressed pellet; silver glue contacts; 50 um gold wire; I-V sweep from 0 to +1 V; measured at 300 K
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| electrical conductivity of desolvated 1 | 1.47 x 10^-13 S cm^-1 | 1.47e-11 S m^-1 | — | Text Exact Reported | 5 · 3.5. Guest tunable electric conductivities · Fig. 5; Fig. S10 |
desolvated 1 pellet · Pellet
I-V curves swept from 0 to +1 V with a temperature step of 10 K; SI Fig. S10 legends show 300-370 K; activation energy extracted from log(sigma)-1/T fit
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| activation energy of desolvated 1 | Ea = 0.41 eV | 0.41 eV | — | Text Rounded Reported | 5 · 3.5. Guest tunable electric conductivities · Fig. S10b |
| temperature-dependent I-V range | 300-370 K | — | — | Figure Axis Range | 6-7 · Supplementary Fig. S10 · Fig. S10c-d |
I2@1 pellet · Pellet
I2@1 from desolvated 1 soaked in 1 mM aqueous I2 for 8 h; pressed pellet; measured at 300 K
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| conductivity enhancement after I2 uptake | two orders conductivity enhancement | — | — | Text Qualitative | 5 · 3.5. Guest tunable electric conductivities · Fig. 5 |
| electrical conductivity of I2@1Marked as a best value within this paper | 1.63 x 10^-11 S cm^-1 | 1.63e-9 S m^-1 | — | Text Exact Reported | 5 · 3.5. Guest tunable electric conductivities · Fig. 5; Fig. S10 |