Electrical Transport — Reversible Molecule Interactions Enable Ultrastretchable and Recyclable Ionogels for Wearable Piezoionic Sensors

3 measurement groups · 10 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

flexible ionogel composition series · Thin Film

Room-temperature conductivity of ionogels with different [EMIM][EtSO4] contents; UiO-66-NH2@PAA content controlled as in Figure 2d.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
conductivity at 20 wt% ionic liquid	10.1 uS cm^-1	0.0000101 S cm^-1	—	Figure Axis Rounded Reported	50029 · 3.2 · Figure 2d
best conductivity at 30 wt% ionic liquidMarked as a best value within this paper	44.1 uS cm^-1	0.0000441 S cm^-1	—	Text Exact Reported	50030 · 3.2 · Figure 2d
conductivity at 40 wt% ionic liquid	13.8 uS cm^-1	0.0000138 S cm^-1	—	Figure Axis Rounded Reported	50029-50030 · 3.2 · Figure 2d

flexible ionogel composition series · Thin Film

Conductivity of ionogels with 30 wt% ionic liquid and varied UiO-66-NH2@PAA content from 0 to 20 wt%.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
conductivity at 0 wt% UiO-66-NH2@PAA	approximately 15 uS cm^-1	0.000015 S cm^-1	visual estimate from plotted point	Visual Estimate Approximate	50029 · 3.2 · Figure 2e
conductivity at 15 wt% UiO-66-NH2@PAA	approximately 26 uS cm^-1	0.000026 S cm^-1	visual estimate from plotted point	Visual Estimate Approximate	50029 · 3.2 · Figure 2e
conductivity at 20 wt% UiO-66-NH2@PAA	approximately 21 uS cm^-1	0.000021 S cm^-1	visual estimate from plotted point	Visual Estimate Approximate	50029-50030 · 3.2 · Figure 2e
conductivity at 5 wt% UiO-66-NH2@PAAMarked as a best value within this paper	approximately 44 uS cm^-1	0.000044 S cm^-1	visual estimate from plotted point	Visual Estimate Approximate	50029-50030 · 3.2 · Figure 2e

recycled ionogel · Thin Film

Recycled ionogels compared before and after solvent remoulding with DMAC.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
recycled ionogel conductivity	20.8 uS cm^-1	0.0000208 S cm^-1	—	Text Exact Reported	50031 · 3.2 · Figure 3d
recycled ionogel breaking elongation	766%	—	—	Text Rounded Reported	50031 · 3.2 · Figure 3c,d
recycled elongation retention	90% of original	—	—	Text Rounded Reported	50031 · 3.2 · Figure 3c