Porosity — In Situ Construction of Amide-Functionalized 2D Conjugated Metal-Organic Frameworks with Multiple Active Sites for High-Performance Potassium-Ion Batteries

2 measurement groups · 6 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

as-synthesised Cu-HBB-MOF black powder · Powder

77 K N2 sorption; degassed at 80 C for 12 h under 10^-5 bar vacuum

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface area	605 m2 g-1	—	—	Text Rounded Reported	p003 / 18340 · Synthesis and Characterization · Figure S13
NLDFT pore size distribution centre	2.47 nm	—	—	Text Rounded Reported	p003 / 18340 · Synthesis and Characterization · Figure S13
total pore volume	Vtotal = 0.58 cm3 g-1	—	—	Visual Estimate Rounded Reported	S19 · Section 6 · Figure S13

as-synthesised Cu-Salphen-MOF black powder · Powder

77 K N2 sorption; degassed at 80 C for 12 h under 10^-5 bar vacuum

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface area	726 m2 g-1	—	—	Text Rounded Reported	p003 / 18340 · Synthesis and Characterization · Figure S13
NLDFT pore size distribution centre	2.54 nm	—	—	Text Rounded Reported	p003 / 18340 · Synthesis and Characterization · Figure S13
total pore volume	Vtotal = 0.64 cm3 g-1	—	—	Visual Estimate Rounded Reported	S19 · Section 6 · Figure S13