TGA/DSC thermal analysis
IL0.5@MOF (0.5:1) · Pellet
Approximately 10 mg sample, 5 deg C min-1 in air, 30-700 deg C, NETZSCH STA 449F3 or SDT 2960 Simultaneous DSC-TGA
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| IL0.5@MOF decomposition temperature T1 | 285 deg C | — | — | SI Table Exact Reported | p002 · Supporting information · Table S2 |
| IL0.6@MOF decomposition temperature T1 | 290 deg C | — | — | SI Table Exact Reported | p002 · Supporting information · Table S2 |
| IL0.8@MOF decomposition temperature T1 | 295 deg C | — | — | SI Table Exact Reported | p002 · Supporting information · Table S2 |
| IL@MOF decomposition temperature T1 | 300 deg C | — | — | SI Table Exact Reported | p002 · Supporting information · Table S2 |
| MOF decomposition temperature T1 | 275 deg C | — | — | SI Table Exact Reported | p002 · Supporting information · Table S2 |
| IL0.5@MOF decomposition temperature T2 | 445 deg C | — | — | SI Table Exact Reported | p002 · Supporting information · Table S2 |
| IL0.6@MOF decomposition temperature T2 | 450 deg C | — | — | SI Table Exact Reported | p002 · Supporting information · Table S2 |
| IL0.8@MOF decomposition temperature T2 | 440 deg C | — | — | SI Table Exact Reported | p002 · Supporting information · Table S2 |
| IL@MOF decomposition temperature T2 | 435 deg C | — | — | SI Table Exact Reported | p002 · Supporting information · Table S2 |
| MOF decomposition temperature T2 | 380 deg C | — | — | SI Table Exact Reported | p002 · Supporting information · Table S2 |
| IL0.5@MOF first-stage water mass loss | 19 % | — | — | SI Table Exact Reported | p002 · Supporting information · Table S1 |
| IL0.6@MOF first-stage water mass loss | 18 % | — | — | SI Table Exact Reported | p002 · Supporting information · Table S1 |
| IL0.8@MOF first-stage water mass loss | 17 % | — | — | SI Table Exact Reported | p002 · Supporting information · Table S1 |
| IL@MOF first-stage water mass loss | 13 % | — | — | SI Table Exact Reported | p002 · Supporting information · Table S1 |
| MOF first-stage water mass loss | 10 % | — | — | SI Table Exact Reported | p002 · Supporting information · Table S1 |
| IL0.5@MOF Zn-MOF-74 decomposition mass loss contribution | 46 % | — | — | SI Table Exact Reported | p002 · Supporting information · Table S1 |
| IL0.6@MOF Zn-MOF-74 decomposition mass loss contribution | 47 % | — | — | SI Table Exact Reported | p002 · Supporting information · Table S1 |
| IL0.8@MOF Zn-MOF-74 decomposition mass loss contribution | 48 % | — | — | SI Table Exact Reported | p002 · Supporting information · Table S1 |
| IL@MOF Zn-MOF-74 decomposition mass loss contribution | 54 % | — | — | SI Table Exact Reported | p002 · Supporting information · Table S1 |
| MOF Zn-MOF-74 decomposition mass loss contribution | 44 % | — | — | SI Table Exact Reported | p002 · Supporting information · Table S1 |
| second TGA decomposition stage range | 275 to 445 deg C | — | — | Text Range | p006 / journal page 6 · 3.1 Physicochemical Characterization · Figure 3; Table S2 |
| first TGA decomposition/water-loss stage upper temperature | water loss up to 100 deg C | — | — | Text Rounded Reported | p006 / journal page 6 · 3.1 Physicochemical Characterization · Figure 3; Table S1 |