Flash-photolysis time-resolved microwave conductivity coupled with transient absorption spectroscopy
Zn-Pn SURMOF-2 thin film · Thin Film
Excitation at 3.49 eV/355 nm; photon density 8.9 x 10^15 photons cm-2; quantum yield from TAS radical cation peak at 510-600 nm
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| activation energy for hopping-like transportMarked as a best value within this paper | ~64 meV | 0.064 eV | — | Text Approximate | 4 · Results and discussion · Fig. 3; Fig. S10-S11 |
| experimental photogenerated hole mobility at 300 KMarked as a best value within this paper | 0.03 cm2 V-1 s-1 | 0.03 cm2 V-1 s-1 | — | Text Rounded Reported | 3 · Results and discussion · Fig. 3 |
| charge carrier generation efficiency Phi at 300 K | 1.02 x 10^-3 | — | — | Text Exact Reported | 3 · Results and discussion · Fig. S8-S9 |
| temperature-dependent FP-TRMC maxima range | from 1.0 x 10^-6 to 3.5 x 10^-6 cm2 V-1 s-1 over 220-300 K | — | — | Text Range | 18 · FP-TRMC/TAS discussion · Fig. 3; Fig. S10 |
| charge carrier generation efficiency Phi at 200 K | 1.31 x 10^-3 | — | — | Text Exact Reported | 18 · FP-TRMC/TAS discussion · Fig. S9-S10 |