Electrochemistry Application — Highly Dispersed MoO2Nanoparticles Confined in N-Doped Porous Carbon Nanosheets for Efficient Hydrogen Evolution in Alkaline Media

4 measurement groups · 9 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

MoO2 NPs@N-C NSs/NF · Electrode

CVs in nonfaradaic region 0.05-0.55 V vs RHE at 10, 30, 40, 50, 60, and 80 mV s-1 in 1.0 M KOH; charging current at 0.3 V.

Geometry: working electrode on nickel foam
Context: Target sample ECSA proxy.
Measurement source: 2 and 5 · Electrochemical Characterizations; Results and Discussion · Figure 3f; Figure S7

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
double-layer capacitance Cdl	about 46.67 mF cm-2	—	—	Text Approximate	5 · Results and Discussion · Figure 3f; Figure S7

MoO2 NPs@N-C NSs/NF · Electrode

Long-term durability at 10 mA cm-2 for 24 h at room temperature; LSV before and after 1000 cycles.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
potential change after 1000 cyclesMarked as a best value within this paper	about 11.4 mV	—	—	Text Approximate	5 · Results and Discussion · Figure 3e
overpotential attenuation at 10 mA cm-2 for 24 hMarked as a best value within this paper	about 2%	—	—	Text Approximate	5 · Results and Discussion · Figure 3d

MoO2 NPs@N-C NSs/NF · Electrode

Three-electrode cell in 1.0 M KOH; SCE reference, carbon rod counter, catalyst loading 0.06 mg cm-2; iR-corrected; 5 mV s-1.

Geometry: working electrode on nickel foam
Context: Compared with NF and MoO2/NF controls.
Measurement source: 2-4 · Electrochemical Characterizations; Results and Discussion · Figure 3a; Figure S6

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
MoO2/NF HER overpotential at 10 mA cm-2	210 mV	—	—	Text Rounded Reported	4 · Results and Discussion · Figure 3a
NF HER overpotential at 10 mA cm-2	250 mV	—	—	Text Rounded Reported	4 · Results and Discussion · Figure 3a
HER overpotential at 10 mA cm-2Marked as a best value within this paper	160 mV at 10 mA cm-2	—	—	Text Rounded Reported	4 · Results and Discussion · Figure 3a

MoO2 NPs@N-C NSs/NF · Electrode

Tafel slopes derived from HER polarisation data in 1.0 M KOH.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
MoO2/NF Tafel slope	154.6 mV dec-1	—	—	Text Rounded Reported	4 · Results and Discussion · Figure 3b
NF Tafel slope	167.9 mV dec-1	—	—	Text Rounded Reported	4 · Results and Discussion · Figure 3b
Tafel slopeMarked as a best value within this paper	92.9 mV dec-1	—	—	Text Rounded Reported	4 · Results and Discussion · Figure 3b