Microscopy Morphology — M-008: A stable and reusable metalorganic framework with high crystallinity applied in the photocatalytic hydrogen evolution and the degradation of methyl orange

2 measurement groups · 8 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

M-008a · Powder

JEOL 6490LV SEM, high vacuum, 20 kV; EDS elemental analysis from Fig. 3.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
EDS carbon content	C 61.86 wt%	—	—	Figure Axis Rounded Reported	4 · SEM characterization · Fig. 3
EDS oxygen content	O 16.10 wt%	—	—	Figure Axis Rounded Reported	4 · SEM characterization · Fig. 3
EDS zinc content	Zn 22.04 wt%	—	—	Figure Axis Rounded Reported	4 · SEM characterization · Fig. 3
SEM grain size	380 nm	—	—	Text Rounded Reported	4 · SEM characterization · Fig. 3; Table 1

M-008b · Powder

JEOL 6490LV SEM, high vacuum, 20 kV; EDS elemental analysis from Fig. 3.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
EDS carbon content	C 62.32 wt%	—	—	Figure Axis Rounded Reported	4 · SEM characterization · Fig. 3
EDS oxygen content	O 12.35 wt%	—	—	Figure Axis Rounded Reported	4 · SEM characterization · Fig. 3
EDS zinc content	Zn 25.31 wt%	—	—	Figure Axis Rounded Reported	4 · SEM characterization · Fig. 3
SEM grain sizeMarked as a best value within this paper	1480 nm	—	—	Text Rounded Reported	4 · SEM characterization · Fig. 3; Table 1