Microscopy Morphology — Morphology Control of Mixed Metallic Organic Framework for High-Performance Hybrid Supercapacitors

3 measurement groups · 6 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Benzoic Acid-80 · Electrode

Benzoic Acid-60/80/100 samples; FESEM and TEM used to determine nanoneedle/nanorod morphology and thickness.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Benzoic Acid-100 nanoneedle/nanorod average thickness	100 nm	—	—	Text Rounded Reported	main p.4 · Results and Discussion · Figure S4
Benzoic Acid-60 nanoneedle/nanorod average thickness	68 nm	—	—	Text Rounded Reported	main p.4 · Results and Discussion · Figure S4
Benzoic Acid-80 electrode thickness	around 27.5 um	—	—	Text Approximate	SI p.4 · Figure S6 discussion · Figure S6
Benzoic Acid-80 nanoneedle/nanorod average thickness	92 nm	—	—	Text Rounded Reported	main p.4 · Results and Discussion · Figure S4

H2BDC-80 · Electrode

H2BDC-60/80/100 samples imaged at different magnifications.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
H2BDC-80 electrode thickness	approximately 95 um	—	—	Text Approximate	SI p.4 · Figure S6 discussion · Figure S6

H3BTC-100 · Electrode

H3BTC-60/80/100 samples imaged at different magnifications.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
H3BTC-100 electrode thickness	35.4 um	—	—	Text Rounded Reported	SI p.4 · Figure S6 discussion · Figure S6