Microscopy Morphology — Tailoring Li-ion Storage and Transport in Two-Dimensional Conjugated Metal-Organic Frameworks via Precise Nitrogen Incorporation

2 measurement groups · 5 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Cu-N2-OHBA bulk powder crystals · Powder

SEM of bulk crystals; HRTEM along layer-stacking and in-plane directions

Atmosphere: ambient/TEM vacuum
Geometry: powder on Si/SiO2 or TEM grid
Context: pristine conductive MOF
Measurement source: 4-6 · Material Synthesis and Characterization · Figures 1b and 2a,c,e

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
HRTEM d-spacing (110)	1.56	—	—	Figure Axis Exact Reported	6 · Figure 2 · Figure 2a
SEM morphology	well-defined rod-shaped crystals with length up to several microns	—	—	Text Qualitative	4 · Material Synthesis and Characterization · Figures 1b, S16

Cu-N4-OHBA bulk powder crystals · Powder

SEM of bulk crystals; HRTEM along layer-stacking and in-plane directions

Atmosphere: ambient/TEM vacuum
Geometry: powder on Si/SiO2 or TEM grid
Context: pristine conductive MOF
Measurement source: 4-6 · Material Synthesis and Characterization · Figures 1c and 2b,d,f

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
HRTEM d-spacing (100)	1.79	—	—	Figure Axis Exact Reported	6 · Figure 2 · Figure 2b
HRTEM d-spacing (101)	1.59	—	—	Figure Axis Exact Reported	6 · Figure 2 · Figure 2b
SEM morphology	well-defined rod-shaped crystals with length up to several microns	—	—	Text Qualitative	4 · Material Synthesis and Characterization · Figures 1c, S17