Measurement evidence
Conductive metal-organic frameworks with wheel-shaped metallomacrocycle subunits as high-performance supercapacitor electrodes · Yan Y., Lin X., Ge J. et al. · Chemical Engineering Journal · 2023 · 143739
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
MWM-1 (Co/2Ni) powder/crystals · Powder
Quantum Design MPMS 6000; temperature and frequency dependent susceptibility, 0 and 1000 Oe DC fields
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| molar susceptibility/spin-state increase | increased nearly by a factor of four | — | nearly | Text Approximate | 7 · Section 3.2 · Fig. 4 |
MWM-1 (Co) powder/crystals · Powder
25-800 C under N2, heating rate 5 C min-1
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| TGA stage 1 mass loss | about 3.60% from 30 to 200 C | — | about | Text Approximate | S1-S10 · Figure S6 text · Figure S6 |
| TGA stage 2 mass loss | about 4.70% from 200 to 305 C | — | about | Text Approximate | S1-S10 · Figure S6 text · Figure S6 |
| TGA stage 3 mass loss | ~59.66% from 305 to 424 C | — | ~ | Text Approximate | S1-S10 · Figure S6 text · Figure S6 |