Spectroscopy — Epitaxial Self-Assembly of Interfaces of 2D Metal-Organic Frameworks for Electroanalytical Detection of Neurotransmitters

4 measurement groups · 12 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Co3(HHTP)2 {100} nanorods on GCE · Electrode

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
C atomic percent in Co nanorods	26	—	—	Figure Axis Approximate	19 · XPS composition · Figure S15
Co atomic percent in Co nanorods	26	—	—	Figure Axis Approximate	19 · XPS composition · Figure S15
O atomic percent in Co nanorods	48	—	—	Figure Axis Approximate	19 · XPS composition · Figure S15

Co3(HHTP)2 {001} oriented film on GCE · Electrode

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
C atomic percent in Co sheets	28	—	—	Figure Axis Approximate	19 · XPS composition · Figure S15
Co atomic percent in Co sheets	16	—	—	Figure Axis Approximate	19 · XPS composition · Figure S15
O atomic percent in Co sheets	56	—	—	Figure Axis Approximate	19 · XPS composition · Figure S15

Ni3(HHTP)2 {001} oriented film on GCE · Electrode

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
C atomic percent in Ni sheets	31	—	—	Figure Axis Approximate	20 · XPS composition · Figure S16
Ni atomic percent in Ni sheets	15	—	—	Figure Axis Approximate	20 · XPS composition · Figure S16
O atomic percent in Ni sheets	54	—	—	Figure Axis Approximate	20 · XPS composition · Figure S16

Ni3(HHTP)2 {100} nanorods on GCE · Electrode

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
C atomic percent in Ni nanorods	38	—	—	Figure Axis Approximate	20 · XPS composition · Figure S16
Ni atomic percent in Ni nanorods	14	—	—	Figure Axis Approximate	20 · XPS composition · Figure S16
O atomic percent in Ni nanorods	48	—	—	Figure Axis Approximate	20 · XPS composition · Figure S16