Other — Nickel(II) Cluster-Based Pillar-Layered Metal-Organic Frameworks for High-Performance Supercapacitors

2 measurement groups · 4 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

as-synthesised Ni-mba-K product · Powder

TA-Q600, N2, 5 deg C min-1, 25-850 deg C.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
decomposition temperature	approximately 300 deg C	—	—	Text Approximate	main p.3 (journal p.17280) · 3.1. Structural Characterization · Figure S2b
TGA weight retention at 850 deg C	68.33%	—	—	Figure Axis Rounded Reported	SI p.S2 · Figure S2 · Figure S2b

as-synthesised Ni-mba-Na black fibrous product · Powder

TA-Q600, N2, 5 deg C min-1, 25-850 deg C.

Temperature: 298-1123
Atmosphere: N2
Geometry: powder
Context: pristine framework
Measurement source: main p.2 (journal p.17279) · 2.2. Structure Characterization · Figure S2b

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
decomposition temperature	approximately 300 deg C	—	—	Text Approximate	main p.3 (journal p.17280) · 3.1. Structural Characterization · Figure S2b
TGA weight retention at 850 deg C	64.01%	—	—	Figure Axis Rounded Reported	SI p.S2 · Figure S2 · Figure S2b