Measurement evidence
Electronically Conductive Metal−Organic Framework With Photoelectric and Photothermal Effect as a Stable Cathode for High-Temperature Photo-Assisted Zn/Sn-Air Battery · Chen J., Yang C., Dong Y. et al. · Carbon Energy · 2026 · e70103
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
as-synthesised Ni2DDA black powder · Powder
Ni content in pristine Ni2DDA powder.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Ni content in Ni2DDA | 31.03 wt% | — | — | Text Exact Reported | p004 · Results and Discussion |
as-synthesised Ni2DDA black powder · Powder
Temperature evolution of Ni2DDA powder under NIR irradiation for 10 s to 10 min.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| temperature after 10 min NIR irradiationMarked as a best value within this paper | 92.5 degC | — | — | Text Exact Reported | p006 · Results and Discussion · Figure 4D-F |
| temperature after 10 s NIR irradiation | 59.2 degC | — | — | Text Exact Reported | p006 · Results and Discussion · Figure 4A |
| temperature after 1 min NIR irradiation | 80.4 degC | — | — | Text Exact Reported | p006 · Results and Discussion · Figure 4C |
| temperature after 2 min NIR irradiation | 85.9 degC | — | — | Text Exact Reported | p006 · Results and Discussion · Figure 4 |
| temperature after 30 s NIR irradiation | 72.3 degC | — | — | Text Exact Reported | p006 · Results and Discussion · Figure 4B |
| temperature after 5 min NIR irradiation | 90.5 degC | — | — | Text Exact Reported | p006 · Results and Discussion · Figure 4 |
as-synthesised Ni2DDA black powder · Powder
TG heating to 800 degC in air; XPS at 25, 40 and 80 degC.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| TG decomposition onset | ~364 degC | — | ~ | Text Approximate | p006 · Results and Discussion · Figure 5E |
| TG residual mass after heating to 800 degC in air | ~21.67% | — | ~ | Text Approximate | p006 · Results and Discussion · Figure 5E |
| Ni valence-state stability up to 80 degC | negligible chemical shifts up to 80 degC | — | — | Text Qualitative | p006-p007 · Results and Discussion · Figure 5F-H |