Electrical Transport — Preparation of hierarchical MOF-5 films using morphology controlled ZnO coatings for temperature dependent optical sensors application

2 measurement groups · 8 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

MOF-5/ZnO nanorod MSM photodetector · Electrode

Dark and 365 nm UV illumination at 290 K and 300 K; bias from -10 to +10 V

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
current density at +10 V under 365 nm illumination, 290 K	about 380 uA cm^-2	—	—	Figure Axis Approximate	7 · Photoelectric properties · Fig. 6a
current density at +10 V under 365 nm illumination, 300 K	about 600 uA cm^-2	—	—	Figure Axis Approximate	7 · Photoelectric properties · Fig. 6b
I-V bias range	-10 to +10 V	—	—	Text Range	3 · Apparatus
I-V curve shape	nonlinear, attributed to Schottky contact between metal and MOF-5/ZnO NR film	—	—	Qualitative Qualitative	7 · Photoelectric properties · Fig. 6a,b

MOF-5/ZnO nanorod MSM photodetector · Electrode

Repeated light/dark cycles under UV illumination at 2 V bias, 285 K and 300 K

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
dark current density during switching at 285 K	about 13.5 uA cm^-2	—	—	Figure Axis Approximate	9 · Photoelectric properties · Fig. 9
illuminated current density during switching at 285 K	about 39 uA cm^-2	—	—	Figure Axis Approximate	9 · Photoelectric properties · Fig. 9
dark current density during switching at 300 K	about 26.5 uA cm^-2	—	—	Figure Axis Approximate	9 · Photoelectric properties · Fig. 9
illuminated current density during switching at 300 K	about 52 uA cm^-2	—	—	Figure Axis Approximate	9 · Photoelectric properties · Fig. 9